Nanoscale Res Lett. 2011; 6(1): 463.
Published online Jul 21, 2011. doi:  10.1186/1556-276X-6-463
PMCID: PMC3211884

Effect of growth temperature on the morphology and phonon properties of InAs nanowires on Si substrates

Abstract

Catalyst-free, vertical array of InAs nanowires (NWs) are grown on Si (111) substrate using MOCVD technique. The as-grown InAs NWs show a zinc-blende crystal structure along a < 111 > direction. It is found that both the density and length of InAs NWs decrease with increasing growth temperatures, while the diameter increases with increasing growth temperature, suggesting that the catalyst-free growth of InAs NWs is governed by the nucleation kinetics. The longitudinal optical and transverse optical (TO) mode of InAs NWs present a phonon frequency slightly lower than those of InAs bulk materials, which are speculated to be caused by the defects in the NWs. A surface optical mode is also observed for the InAs NWs, which shifts to lower wave-numbers when the diameter of NWs is decreased, in agreement with the theory prediction. The carrier concentration is extracted to be 2.25 × 1017 cm-3 from the Raman line shape analysis. A splitting of TO modes is also observed.

PACS: 62.23.Hj; 81.07.Gf; 63.22.Gh; 61.46.Km

Introduction

Semiconductor nanowires (NWs) have been intensively studied in the last decade due to their novel physical properties and potential applications in high-performance devices, such as field-effect transistors, lasers, photodetectors, and photovoltaic devices [1-5]. Such NWs are usually grown through vapor-liquid-solid mode where metal nanoparticles (Au, Ni, or other metals) act as catalysts [6-9]. However, for certain materials the metal catalysts can result in unintentional incorporation into pure crystalline NWs, which causes serious problems for materials doping and limits their device applications. In order to avoid the contamination from Au and other metal atoms, it is highly preferred that NWs can be grown without catalysts.

On the other hand, one of the most attracting features of NWs is that lattice mismatch or strain in NWs can be significantly relaxed due to their high surface/volume ratio and small lateral size. This can be used to realize one of the dreams in semiconductor community--integration of III-V semiconductor on Si platform [10,11], which presents a big challenge due to the significant lattice mismatch and differences in coefficient of thermal expansion between Si and III-V materials. The integration of III-V semiconductor on Si will allow people to take advantage of both the key features of Si like low cost and mature processing technology and those of III-V semiconductor like direct bandgap and high-quality heterostructure growth. Among the III-V semiconductors, InAs NWs possess excellent electron transport properties such as high bulk mobility, small effective mass, and low ohmic contact resistivity, which can be used for preparing high-performance electronic devices such as high mobility transistor [12,13].

Though some work has been done on catalyst-assisted InAs NWs [8,14], little work has been devoted to catalyst-free InAs NWs, especially on Si substrates [5,15,16]. In this paper, we present a study on the catalyst-free synthesis and phonon properties of InAs NWs on Si substrates. By varying the growth temperature, InAs NWs with different diameters were grown on Si substrates. The phonon properties of the InAs NWs are investigated using Raman scattering characterization. The effects of growth temperature on the frequency shift of longitudinal optical (LO), transverse optical (TO), and surface optical (SO) modes are analyzed. Furthermore, a splitting of TO modes also is observed and discussed.

Experimental details

Vertical InAs NWs arrays were grown on n-type Si (111) substrates in a close-coupled showerhead metal-organic chemical vapor deposition (MOCVD) system (Thomas Swan Scientific Equipment, Ltd., Cambridge, UK) at a pressure of 100 Torr. Trimethylindium (TMIn) and AsH3 were used as precursors and ultra-high purity H2 as carrier gas. First, Si substrates were cleaned (ultrasonicate in trichloroethylene, acetone, isoproponal, and deionized water sequentially) and etched in buffered oxide etch solution (BOE, six parts 40% NH4F and one part 49% HF) for 30 s to remove the native oxide, and then rinsed in deionized water for 15 s and dried with N2. Then, the substrates were loaded into the MOCVD chamber for growth. The substrates were heated up to the growth temperature ranging from 530°C to 570°C, and after 5-min stabilization time, the growth was initiated by simultaneous introducing TMIn (2 × 10-6 mole/min) and AsH3 (2 × 10-4 mole/min) into the reactor chamber for 7 min. After the growth, InAs NWs were cooled down with the protection of AsH3 flow. To obtain more understanding about the controlled growth of catalyst-free InAs NWs on Si, InAs NWs were grown at various temperatures ranging from 530°C to 570°C, i.e., 530°C for sample A, 550°C for sample B and 570°C for sample C. The morphology of InAs NWs was characterized by field emission scanning electron microscopy (S-4800, Hitachi, Tokyo, Japan) and high-resolution transmission electron microscopy (HRTEM, Tecnai F20, 200 keV; FEI, Eindhoven, Netherlands). Raman scattering measurements were performed in backscattering geometry at room temperature with a Jobin Yvon HR800 confocal micro-Raman spectrometer (Horiba Ltd., Longjumeau, France). Scattering configuration An external file that holds a picture, illustration, etc.
Object name is 1556-276X-6-463-i1.gif (An external file that holds a picture, illustration, etc.
Object name is 1556-276X-6-463-i2.gif) was adopted. The samples were excited by the 514.5 nm line of an Ar-ion laser to a 1 µm spot on the surface with an excitation power of 0.05 mW.

Results and discussion

Figure Figure11 shows the SEM images of samples A, B, and C. It is observed that vertical and uniform InAs NWs with hexagonal cross sections are obtained in all the three samples. With few exceptions, all InAs NWs are grown along the < 111 > direction, which is perpendicular to Si substrate surface. No large base islands are observed at the base area surrounding NWs' root, which is different from the case of catalyst-assisted growth of NWs where large base islands are usually observed [9]. This suggests a different growth mechanism for catalyst-free InAs NWs compared with catalyst-assisted InAs NWs. According to previous work [5], the large lattice mismatch between InAs and Si could be the driving force for such catalyst-free NW growth. InAs clusters/islands first nucleate in Volmer-Weber mode on Si, where uniform film growth is prohibited due to the large interfacial energy. Then, to relax the strain energy in the system, the InAs material is preferred to grow vertically and form NWs. The few large InAs islands and non-vertical InAs NWs observed in sample A, B, and C can be explained by the reoxidation in the system, which provides nucleation sites and reactant sinks and also assist in the growth of larger InAs islands and non-vertical NWs [5,16].

Figure 1
FE-SEM (45° tilted view) and TEM images of the InAs nanowires grown for 7 min on Si(111) substrates. Nanowires were (a) grown at 530°C (sample A), (b) grown at 550°C (sample B), (c) grown at 570°C (sample C); (d) low-resolution ...

Table Table11 summarizes the statistical size information of InAs NWs in the three samples. With increasing growth temperature from 530°C to 570°C, the average density of InAs NWs decreases from 8 to 4 μm-2, while the average diameter of InAs NWs increases from 35 to 70 nm. Meanwhile, the average length of InAs NWs also decreased from 2 to 1.2 μm with increasing growth temperature. The change of NW density with increasing growth temperature has also been observed in InAs NWs on InP (111) B substrates [17]. The NWs density is mainly governed by the nucleation kinetics of clusters on the surfaces, and the NW density ρ is determined by the materials deposition rate and growth temperature: ρ [proportional, variant] R/D(T), with R being the material deposition rate and D(T) being the temperature-dependent coefficient of surface diffusion. Therefore, the NW density will decrease with increasing growth temperature. Such change also indicates that InAs clusters or cluster-related nucleation is initiated at the pre-stages of wire growth. At proper temperatures, these clusters grow anisotropically and form one-dimensional NWs. But at lower temperatures, only a part of the clusters follow the anisotropic growth mechanism, others grow by isotropic expansion resulting in larger InAs islands. Indeed, as shown in Figure Figure1a1a more InAs large islands are observed in sample A, where InAs NWs are grown at 530 C. Apart from the decreased NW density, the aspect ratio (length/width) of InAs NWs decreases significantly from 57.1 to 17.1 with increasing temperature from 530°C to 570°C. At higher temperatures, the radial growth on the side facets becomes more significant, leading to the formation of NWs with large diameter and small length, and thus small aspect ratio.

Table 1
Growth parameters and morphology statistics of InAs NWs grown in sample A, B, and C.

To study the structural properties of InAs NWs, HRTEM measurements were carried out. Figure Figure1d1d shows the typical HRTEM image of InAs NWs (sample B). It is observed that the InAs NW is uniform in diameter. It should be noted that alternative dark and bright contrast bands are observed, which can be attributed to the rotation twins and stacking faults. Figure Figure1e1e shows the HRTEM image of sample B with its inset showing the fast Fourier transforms (FFTs) image. The HRTEM image combining with FFT image indicates that the InAs NWs has a cubic, zinc blend structure and grows along the < 111 > direction normal to the Si (111) substrate. Such rotation twins and stacking faults are formed by random stacking of the closest-packed planes during crystal growth, which have also been observed in III-V NWs grown along the < 111 > direction [18,19].

Figure Figure2a2a shows the Raman spectrum of InAs NWs in sample B measured with incident laser beam parallel to the c-axis of NWs. Three main scattering peaks are observed, which are located around 237.9, 230.0, and 216.2 cm-1, respectively. To probe the origin of these three Raman peaks, Raman measurements are also performed on bulk InAs (111) substrate for comparison, the spectrum of which is shown in Figure Figure2b.2b. For bulk InAs materials, two Raman peaks are clearly observed: one is located around 241.0 cm-1, the other around 218.7 cm-1, which can be attributed to the LO and TO phonon modes of bulk InAs. Therefore, Raman peaks located at 237.9 and 216.2 cm-1 in Figure Figure2a2a can be attributed to the LO and TO phonon mode of InAs NWs. Except the downshift of their phonon frequency relative to InAs bulk material, the LO and TO phonon peaks of InAs NWs also show a larger full width at half maximum. To explain such frequency downshift and line-width broadening of LO and TO phonon peaks of InAs NWs, three possible reasons should be taken into account. One is the small lateral size of InAs NWs. According to the "spatial correlation" model proposed by Richter et al. [20] and Tiong et al. [21], and also generalized by Campbell and Faucher et al. [22], the reduction in physical dimension of materials can lead to a downshift of phonon frequency and a broadening of the LO phonon peak due to the strong quantum confinement and the relaxation of q = 0 selection rule. However, the diameter of our InAs NWs is very large (> 20 nm) and shows almost no quantum confinement effect, which cannot explain the observed downshift in phonon frequency of LO and TO phonon peaks. Another one is the thermal anharmonicity effect caused by temperature change. Anharmonicity entails the participation of phonons at frequencies multiple of the fundamental in the scattering events [23]. Such anharmonic effects become prominent at higher temperatures due to the larger extent of lattice vibrations, and are irrespective of the longitudinal or transverse character of the phonon modes. Theoretically, an increase in temperature can induce both line-width broadening and frequency downshift of phonon peaks. However, our Raman spectra are measured under a low laser excitation power of 0.05 mW, where the heating effect can be ignored. The last one is the existence of structural defects in NWs. As indicated by the work on GaAs and InAs NWs grown on SiO2 and GaAs substrates, defects can cause a frequency downshift and line-width broadening to the phonon peaks [8]. As shown by the HRTEM study, defects like rotation twins and stacking faults exist in the samples, which might relax the q = 0 selection rule and lead to the frequency downshift and line-width broadening of the phonon peaks.

Figure 2
Raman spectra of InAs nanowires and temperature-dependent Raman shift. (a) Micro-Raman spectra of InAs nanowires with an average diameter of 42 nm. The black line is the recorded data while the lighter colored (green) lines are results from a multiple ...

As shown in Figure Figure2,2, beside LO and TO phonon peaks, there is another phonon peak centered around 230.0 cm-1, which can be attributed to the SO phonons. Such SO phonon modes have also been observed in GaP, ZnS, GaAs, and InAs NWs [24-32]. According to the model proposed by Ruppin and Englman [27], the frequency of SO phonon mode in a cylinder NW can be calculated by the expression

equation image
(1)
equation image
(2)

Where ωSO is surface phonon frequency; ωTO is TO phonon frequency; ωp is the screened ion plasma frequency, ε0 and εare static and dynamic dielectric constants, respectively; εm is dielectric constant of the surrounding medium and ρ is expressed as:

equation image
(3)

where Kn(x) and In(x) (n = 0,1) are the modified Bessel functions and x = qr (r being the radius of the NW). For InAs materials, the following parameters are used for the calculation: ε0 = 13.9, ε= 11.6, εm = 1 (the NWs are immersed in air) [15], ωTO = 216.7 cm-1. The plasmon frequency ωp can be related to the free carriers concentration (n) and effective electron mass of InAs (m* = 0.024me) [15],

equation image
(4)

Vice versa, the free carrier concentration can be calculated if the frequency of SO phonon mode and the size of the NWs are known. Here, the free carrier concentration in sample B is estimated to be 2.25 × 1017 cm-3using the measured diameter (42 nm) and SO phonon frequency (230.0 cm-1). This result is close to the value obtained through electrical measurements in [5]. This high free carrier concentration in the InAs NWs might be caused by the unintentional doping due to carbon background incorporation [5]. To get more understanding of this SO phonon mode in InAs NWs, temperature-dependent Raman measurements are also performed on the InAs NWs in sample B, the results are shown in Figure Figure2c.2c. It is observed that the SO phonon peak shifts to lower frequency with increasing the temperature, which is similar to the temperature behavior of the LO and TO mode of InAs NWs, and can be explained by the lattice expansion in NWs. It should be noted that though the SO feature is not apparent at high temperatures (> 173 K) the free carrier concentration should still be around the value (2.25 × 1017 cm-3) at low temperatures considering the fact that the free carrier concentration induced by unintentionally doping is much higher than that of intrinsic carrier in InAs materials (~1 × 1015 cm-3).

Apart from sample B, Raman experiments are also performed on sample A and C. Figure Figure33 shows Raman spectra of InAs NWs measured with incident laser beam parallel to the c-axis of NWs at room temperature. As stated above, the phonon peaks on low energy side of LO phonon modes are from SO phonon modes. Obviously, the SO phonon peak shifts toward lower energy side with reducing NWs' diameter. More interestingly, for InAs NWs with smaller diameters (larger surface-to-volume ratio), the SO phonon mode can be more clearly distinguished. These features further indicate that the Raman peak located between TO and LO phonon peaks can, indeed, be attributed to the scattering from surface phonons. According to the model stated above, the phonon frequency of SO mode can be calculated according to the diameter of NWs. Figure Figure3b3b shows the calculated phonon frequency of SO mode in InAs NWs with various diameters and the experimentally measured phonon frequency of SO mode of InAs NWs in sample A, B, and C. Obviously, the experimental values agree well with the theoretical values, confirming the SO mode origin of the Raman peak between LO and TO phonon peaks.

Figure 3
Raman spectra of InAs NWs measured with different average diameter and theoretical prediction. (a) Raman spectra from InAs NWs with average diameters from 35 nm (red), 42 nm (black), and 70 nm (blue). The lighter colored (green) lines are results from ...

Figure Figure44 shows the Raman spectra of InAs NWs with a diameter of 42 nm (sample B) measured with the incident laser beam both parallel An external file that holds a picture, illustration, etc.
Object name is 1556-276X-6-463-i7.gif and perpendicular An external file that holds a picture, illustration, etc.
Object name is 1556-276X-6-463-i8.gif to the c-axis of NWs. Note that the laser excitation power used for measuring Raman spectra in Figure Figure44 is 0.25 mW. Compared with the TO peak measured with incident laser beam parallel to c-axis of NWs, the TO peak measured with incident laser beam perpendicular to c-axis of NWs shifts to lower frequency with asymmetric broadening, where a weak shoulder peak appears at the lower energy side of TO mode. This indicates a possible splitting of TO mode, giving rise to A1 (TO) mode reported [31]. A more detailed study on the splitting as a function of the NW crystal structure, strain, diameter, and length is currently under way.

Figure 4
Raman spectra of InAs NWs recorded parallel and perpendicular to the c-axis. (a) Raman spectra of as-grown vertical aligned InAs NWs (sample B) recorded in backscattering geometry parallel to the c-axis, (b) Raman spectra of InAs NWs recorded perpendicular ...

Conclusion

To summarize, the catalyst-free, growth, and phonon properties of InAs NWs on Si (111) substrates are investigated in detail in this paper. Both the density and the length of InAs NWs decrease with increasing growth temperatures, while the diameter of InAs NWs increases with increasing growth temperature, suggesting that the catalyst-free growth of InAs NWs are governed by the nucleation kinetics in the system. The LO and TO mode of InAs NWs both present a phonon frequency smaller lower than those of InAs bulk materials, which is speculated to be mainly caused by the defects in the NWs. Apart from LO and TO phonon modes, a SO mode is also observed for the InAs NWs, the signal feature of which becomes more prominent with reducing the diameter of NWs due to the increased surface/volume ratio. A splitting of transverse optical (TO) modes also is observed.

Abbreviations

NWs: nanowires; MOCVD: metal-organic chemical vapor deposition; LO: longitudinal optical; TO: transverse optical; SO: surface optical; SEM: scanning electron microscopy; HRTEM: high-resolution transmission electron microscopy.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

TL carried out the experimental analysis and drafted the manuscript. YC carried out the experimental design. WL and XZ participated in the experimental analysis. SL carried out the growth and optimization of InAs NWs. YH participated in the experimental measurement. LW participated in its design and coordination. TY and ZW participated in the experimental design. All authors read and approved the final manuscript.

Acknowledgements

The work was supported by the National Natural Science Foundation of China (No. 60625402 and 60990313), and the 973 program.

References

  • Yan RX, Gargas D, Yang PD. Nanowire photonics. Nature Photonics. 2009;3:569. doi: 10.1038/nphoton.2009.184. [Cross Ref]
  • Lu W, Lieber CM. Semiconductor nanowires. J Phys D. 2006;39:R387. doi: 10.1088/0022-3727/39/21/R01. [Cross Ref]
  • Patolsky F, Lieber CM. Nanowire nanosensors. Mater Today. 2005;8:20.
  • Li Y, Qian F, Xiang J, Lieber CM. Battery betters performance energy generation. Mater Today. 2006;9:18.
  • Wei W, Bao XY, Soci C, Ding Y, Wang ZL, Wang DL. Direct Heteroepitaxy of vertical InAs nanowires on Si substrates for broad band photovoltaics and photodetection. Nano Lett. 2009;9:2926. doi: 10.1021/nl901270n. [PubMed] [Cross Ref]
  • Tomioka K, Motohisa J, Hara S, Fukui T. Control of InAs nanowire growth directions on Si. Nano Lett. 2008;8:3475. doi: 10.1021/nl802398j. [PubMed] [Cross Ref]
  • Zhang RQ, Lifshitz Y, Lee ST. Oxide-assisted growth of semiconducting nanowires. Adv Mater. 2003;15:635. doi: 10.1002/adma.200301641. [Cross Ref]
  • Begum N, Piccin M, Jabeen F, Bais G, Rubini S, Martelli F, Bhatti AS. Structural characterization of GaAs and InAs nanowires by means of Raman spectroscopy. J Appl Phys. 2008;104:104311. doi: 10.1063/1.3026726. [Cross Ref]
  • Dayeh SA, Yu ET, Wang DL. III-V nanowires growth mechanism: V/III ratio and temperature effects. Nano Lett. 2007;7:2486. doi: 10.1021/nl0712668. [PubMed] [Cross Ref]
  • Mokkapati S, Jagadish C. III-V Compound SC for optoelectronic devices. Mater Today. 2009;12:22.
  • Tomioka K, Motohisa J, Hara S, Hiruma K, Fukui T. GaAs/AlGaAs core multishell nanowire-based light-emitting diodes on Si. Nano Lett. 2010;10:1639. doi: 10.1021/nl9041774. [PubMed] [Cross Ref]
  • Adachi S. Properties of Group-IV, III-V and II-VI semiconductors. New York: Wiley; 2005.
  • Dayeh SA, Aplin D, Zhou XT, Yu PKL, Yu ET, Wang DL. High electron mobility InAs nanowire field-effect transistors. Small. 2007;3:326. doi: 10.1002/smll.200600379. [PubMed] [Cross Ref]
  • Xu XX, Yu KH, Wei W, Peng B. Raman scattering in InAs nanowires synthesized by a solvothermal route. Appl Phys Lett. 2006;89:253117. doi: 10.1063/1.2422897. [Cross Ref]
  • Cantoro M, Klekachev AV, Nourbakhsh A, Soree B, Heyns MM, Gendt SD. Eur Phys J B. 2011. p. 423. [Cross Ref]
  • Cantoro M, Wang G, Lin HC, Klekachev AV, Richard O, Bender H, Kim TG, Clemente F, Adelmann C, Veen MH, Brammertz G, Degroote S, Leys M, Caymax M, Heyns MM, Gendt SD. Large-area, catalyst-free heteroepitaxy of InAs nanowires on Si by MOVPE. Phys Status solidi A. 2011;208:129. doi: 10.1002/pssa.201026396. [Cross Ref]
  • Mandl B, Stangl J, Martensson T, Mikkelsen A, Eriksson J, Karlsson LS, Bauer G, Samuelson L, Seifert W. Au-free epitaxial growth of InAs nanowires. Nano Lett. 2006;6:1817. doi: 10.1021/nl060452v. [PubMed] [Cross Ref]
  • Woo RL, Xiao R, Kobayashi Y, Gao L, Goel N, Hudait K, Mallouk TE, Hicks RF. Effect of twinning on the photoluminescence and photoelectrochemical properties of indium phosphide nanowires grown on silicon (111) Nano Lett. 2008;8:4664. doi: 10.1021/nl802433u. [PubMed] [Cross Ref]
  • Bao JM, Bell DC, Capasso F. Optical properties of rotationally twinned InP nanowire heterostructures. Nano Lett. 2008;8:836. doi: 10.1021/nl072921e. [PubMed] [Cross Ref]
  • Richter H, Wang ZP, Ley L. The one phonon Raman spectrum in microcrystalline silicon. Solid State Commun. 1981;39:625. doi: 10.1016/0038-1098(81)90337-9. [Cross Ref]
  • Tiong KK, Amirtharaj PM, Pollak FH, Aspnes DE. Effects of As ion implantation on the Raman spectra of GaAs: "Spatial correlation" interpretation. Appl Phys Lett. 1984;44:122. doi: 10.1063/1.94541. [Cross Ref]
  • Campbell IH, Fauchet PM. The effect of microcrystal size and shape on the one phonon Raman spectra of crystalline semiconductors. Solid State Commum. 1986;58:739. doi: 10.1016/0038-1098(86)90513-2. [Cross Ref]
  • Balkanski M, Wallis RF, Haro E. Anharmonic effects in light scattering due to optical phonons in silicon. Phys Rev B. 1983;28:1928. doi: 10.1103/PhysRevB.28.1928. [Cross Ref]
  • Adu KW, Xiong Q, Gutierrez HR, Chen G, Eklund PC. Raman scattering as a probe of phonon confinement and surface optical modes in semiconducting nanowires. Appl Phys A: Mater Sci Process. 2006;85:287. doi: 10.1007/s00339-006-3716-8. [Cross Ref]
  • Spirkoska D, Abstreiter G, Morral AF. Size and environment dependence of surface phonon modes of gallium arsenide nanowires as measured by Raman spectroscopy. Nanotechnology. 2008;19:435704. doi: 10.1088/0957-4484/19/43/435704. [PubMed] [Cross Ref]
  • Begum N, Bhatti AS, Jabeen F, Rubini S, Martelli F. Lineshape analysis of Raman scattering from LO and SO phonons in III-V nanowires. J Appl Phys. 2009;106:114317. doi: 10.1063/1.3267488. [Cross Ref]
  • Ruppin R, Englman R. Optical phonons of small crystals. Rep Prog Phys. 1970;33:149. doi: 10.1088/0034-4885/33/1/304. [Cross Ref]
  • Hayashi S, Kanamori H. Raman scattering from the surface phonon mode in GaP microcrystals. Phys Rev B. 1982;26:7079. doi: 10.1103/PhysRevB.26.7079. [Cross Ref]
  • Gupta R, Xiong Q, Mahan GD, Eklund PC. surface optical phonons in gallium phosphide nanowires. Nano Lett. 2003;3:1745. doi: 10.1021/nl034842i. [Cross Ref]
  • Xiong Q, Wang JG, Reese O, Voon LC, Eklund PC. Raman scattering from surface phonons in rectangular cross-sectional w-ZnS nanowires. Nano Lett. 2004;4:1991. doi: 10.1021/nl048720h. [Cross Ref]
  • Zardo I, Conesa-Boj S, Peiro F, Morante JR, Arbiol J, Uccelli E, Abstreiter G, Morral AF. Raman spectroscopy of wurzite and zinc-blende GaAs nanowires: Polarization dependence, selection rules, and strain effects. Phys Rew B. 2009;80:245324.
  • Jeganathan K, Debnath PR, Meijers R, Stoica T, Calarco R, Grutzmacher D, Luth H. Raman scattering of phonon-plasmon coupled modes in self-assembled GaN nanowires. J Appl Phys. 2009;105:123707. doi: 10.1063/1.3148862. [Cross Ref]

Articles from Nanoscale Research Letters are provided here courtesy of Springer
PubReader format: click here to try

Formats:

Related citations in PubMed

See reviews...See all...

Cited by other articles in PMC

See all...

Links

  • PubMed
    PubMed
    PubMed citations for these articles

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...