Nanoscale Res Lett. 2011; 6(1): 359.
Published online Apr 21, 2011. doi:  10.1186/1556-276X-6-359
PMCID: PMC3211449

Photoluminescence of spray pyrolysis deposited ZnO nanorods

Abstract

Photoluminescence of highly structured ZnO layers comprising well-shaped hexagonal rods is presented. The ZnO rods (length 500-1,000 nm, diameter 100-300 nm) were grown in air onto a preheated soda-lime glass (SGL) or ITO/SGL substrate by low-cost chemical spray pyrolysis method using zinc chloride precursor solutions and growth temperatures in the range of 450-550°C. We report the effect of the variation in deposition parameters (substrate type, growth temperature, spray rate, solvent type) on the photoluminescence properties of the spray-deposited ZnO nanorods. A dominant near band edge (NBE) emission is observed at 300 K and at 10 K. High-resolution photoluminescence measurements at 10 K reveal fine structure of the NBE band with the dominant peaks related to the bound exciton transitions. It is found that all studied technological parameters affect the excitonic photoluminescence in ZnO nanorods.

PACS: 78.55.Et, 81.15.Rs, 61.46.Km

Introduction

ZnO is a semiconductor material for various photonic and electrical applications. ZnO shows a unique set of physical and chemical properties, such as a wide band gap (3.37 eV), large exciton binding energy (60 meV) at room temperature, radiation hardness [1], piezoelectricity and photoelasticity [2] and surface chemistry sensitive to environment. Zinc oxide nanostructured layer comprizing nanorods, further denoted as ZnO nanorod layer (ZnONRL), is a material with large effective surface area, suitable for short-wavelength devices, such as ultraviolet (UV) light-emitting diodes (LED) [3,4], UV nanolaser arrays [5], UV photodetectors [6], field emitters [7], UV protectors-filters [8], and chemical sensors [9,10]. As a passive layer with light-trapping properties, ZnONRL can be used as an antireflection coating on silicon solar cells [11], surface-enhancing window layer in the second generation solar cells with extremely thin inorganic absorber layer (ETA) [12] or with dye-sensitized solar cells (DSSC) [13]. The chemical spray pyrolysis (CSP)-deposited ZnONRL was used in ETA solar cells showing energy conversion efficiency of 4.2% [14].

For many of such devices, a large-scale, low-cost fabrication of high optical and crystalline quality ZnO is desirable. Low-temperature chemical synthesis methods can provide large scale and low-cost fabrication. Photoluminescence (PL) is a very sensitive and an effective method to identify the dominant recombination mechanism and defects in materials. However, according to PL study, the as-deposited ZnONRL grown via a low-temperature wet-chemical methods (chemical bath, electrodeposition, hydrothermal growth) do not show a high excitonic to visible emission intensity ratio at 300 K (room temperature), indicating a high defect concentration in these samples [15-21]. The PL properties of ZnONRL deposited by the wet-chemical methods can be improved by post-growth annealing at high temperatures of 200-850°C in forming gas or vacuum environment [15,17-19,21].

In this study, strong excitonic PL is observed in the as-deposited ZnONRL, grown via CSP at growth temperatures up to 550°C from zinc chloride (ZnCl2) solutions. CSP technique is a template- and catalyst-free method, allowing fast and low-cost deposition of ZnONRL [22]. According to XRD, ZnONRL comprise c-axis (002)-oriented, hexagonal rods of pure ZnO wurtzite phase with aspect ratio up to 30 [23,24]. The aim of this work is to study the variation in the PL response due to different growth parameters used for the CSP-deposited ZnONRL. As a result, the PL properties were found to depend on the growth temperature, substrate type, spray rate, and the solvent type. The correlation between the electrical and the photoluminescence properties of the CSP-deposited ZnONRL were reported earlier [25]. Our previous studies on the CSP-deposited ZnONRL were focused on the development of the ZnONRL [22-24], no specific study on the PL of the CSP-deposited ZnONRL was reported until now.

Experimental

The ZnONRL were deposited by pneumatic CSP method in air at growth temperatures (TG) of 480°C, 530°C, 550°C using zinc chloride (ZnCl2) precursor solutions. Two kind of substrates were used: soda-lime glass (SGL) and commercial indium tin oxide-covered glass (ITO/SGL). The growth temperature TG was controlled through the temperature of a molten tin bath used to obtain uniform heating of the substrate. Other deposition parameters were varied in the following: Three discrete values were used for the spray rate (v): 1.2, 2.2, and 6.2 ml/min. Two kinds of solvents for ZnCl2 were used: H2O and alcoholic solvent (H2O + ethanol, in ratio of 2:3 by volume), the volume of spray solution was 50 ml. The concentration of ZnCl2 in the spray solution was kept constant in the presented series ranging from 0.05 mol/L ( Effect of the substrate on PL properties of ZnONRL and Effect of the spray rate on PL properties of ZnONRL sections) to 0.1 mol/L (General properties of ZnONRL, Effect of the growth temperature on PL properties of ZnONRL, and Effect of solvent type on PL properties of ZnONRL sections). The acidity of the solution was kept at pH = 5. The studied samples were as grown. XRD measurements were performed on a Rigaku Ultima IV diffractometer with Cu Kα radiation (λ = 1.5406 Å) using the silicon strip detector D/teX Ultra.

The photoluminescence (PL) measurements of ZnONRL were made at room temperature (T = 300 K) and at T = 10 K in a closed-cycle He cryostat (Janis). He-Cd laser (325 nm) was used as an excitation source, the excitation intensity was approximately 0.5 mW/mm2. The luminescence emission in the energy region of 1.45-3.45 eV was dispersed by a computer-controlled Carl Zeiss SPM-2 monochromator (f = 0.4 m) equipped with a prism and detected by FEU-79 photomultiplier with a lock-in amplifier. High-resolution LabRam Horiba Yvon HR 800 spectrometer and CCD-detector were used in the region of 3.30-3.40 eV for a closer study of the PL of ZnONRL in UV-region. The same apparatus was used for the Raman spectroscopic studies. Zeiss EVO-MA15 apparatus was used for the scanning electron microscopic (SEM) and the energy dispersive spectroscopic (EDS) study of the ZnONRL. The apparatus was equipped with the Oxford Instruments PentaFet x3 spectrometer using the INCA Energy EDS system at accelerating voltage of 7 kV.

Results and discussion

General properties of ZnONRL

Typical XRD pattern of sprayed ZnONRL is presented in Figure Figure1.1. According to XRD, the as-grown ZnONRL are highly c-axis-oriented hexagonal (wurtzite) ZnO structures. The Raman spectrum of as-deposited ZnONRL is presented in Figure Figure2.2. Raman peaks located at 99 and 438 cm-1 with a fitted excitonic peak widths (FWHM) of 1.2 and 6.1 cm-1, respectively, are dominant ones. Raman peaks at 99, 438, and 379 cm-1 are attributed to the E2(low), E2(high), and A1(TO) Raman modes of wurtzite phase of ZnO, respectively [26]. The Raman peak at approximately 580 cm-1 which is correlated to VO and/or Zni defects [27] is not observed. The peaks at 128, 330, and 1,153 cm-1 are due to the second order or multiple phonon scattering of the Raman modes of the ZnO wurtzite structure, observed by other authors as well [28]. The sharp Raman peaks characteristic of the wurtzite phase and the absence of defect-induced Raman peaks is an indication of a high-quality crystalline material. According to EDS analysis, the O/Zn atomic ratio in ZnONRL is ca. 1.5. The excess of oxygen (compared to the stoichiometric ZnO) as well as the presence of In, Sn, and Si signal in the EDS spectra (not presented), originates from the ITO/SGL substrate. Other elements are not detected by the EDS.

Figure 1
XRD pattern of ZnO nanorod layer deposited by chemical spray pyrolysis. The layer was deposited onto ITO/SGL substrate at growth temperature of 550°C, using aqueous solution. SEM image of the corresponding ZnO nanorod sample is presented in Figure ...
Figure 2
Raman spectrum of ZnO nanorod layer deposited by chemical spray pyrolysis. The layer was deposited onto ITO/SGL substrate at growth temperature of 550°C, using aqueous solvent. SEM image of the corresponding ZnO nanorod sample is presented in ...

SEM surface images of ZnONRL grown onto ITO/SGL substrate are presented as Figure Figure3.3. The ZnONRL deposited from aqueous solution of ZnCl2 (0.1 mol/L) at TG = 550°C is composed of separately standing ZnO crystals with a diameter of 100-300 nm and length of ca. 800 nm, see Figure Figure3a.3a. When grown at a lower temperature of TG = 480°C using aqueous solutions, the rod-like shape of the crystals is not well-developed (Figure (Figure3b)3b) as also shown in our earlier study [22]. However, the deposition of an alcoholic solution at TG = 480°C results in well-developed hexagonal rods with a diameter of ca. 100-200 nm and length of ca. 700-800 nm (see Figure Figure3c).3c). This result indicates that the spray of an alcoholic solution allows to obtain ZnONRL composed of rods with high aspect ratio at lower substrate temperature compared to the spray of aqueous solution.

Figure 3
SEM images of ZnO nanorod layers deposited by chemical spray pyrolysis. The layers (a, b, c) were deposited onto ITO/SGL substrate at growth temperature of 550°C (a) or 480°C (b, c) using aqueous (a, b) or alcoholic solutions (c) at similar ...

The PL spectra of the best ZnONRL samples show a dominant near band edge (NBE) emission at T = 10 K and at T = 300 K, see Figure Figure44 (further discussion in Effect of the substrate on PL properties of ZnONRL, Effect of the growth temperature on PL properties of ZnONRL, Effect of the spray rate on PL properties of ZnONRL, and Effect of solvent type on PL properties of ZnONRL sections). The NBE peak positions were determined by fitting the spectra with the Lorentz distribution using the Fityk curve-fitting freeware. The NBE peak measured at T = 300 K is due to free exciton transition. High-resolution PL measurements at T = 10 K reveal four transitions due to bound excitons: a prevailing exciton peak at 3.358-3.360 eV, two other exciton peaks at 3.363 eV and 3.368-3.370 eV, a peak of the two electron transition at 3.334-3.335 eV and the free exciton peak at 3.378 eV [26,29-32]. The exciton peak at ca. 3.360 eV, which is attributed to a donor-related transition by many authors [26,29-32], is present as the dominant transition, irrespective of the deposition conditions.

Figure 4
Photoluminescence spectra at 10 K of the spray pyrolysis-deposited ZnO nanorod layers. The layers were deposited from aqueous solution onto SGL or ITO/SGL substrates, illustrated by spectrum A and B, respectively. The growth temperature (550°C) ...

Effect of the substrate on PL properties of ZnONRL

The PL spectra of ZnONRL deposited at TG of 550°C onto the SGL and the ITO/SGL substrates, are presented as Figure Figure4.4. We can see a drastic reduction of the red band intensity at 10 K in case of ZnONRL on ITO/SGL substrate. In addition, the green PL emission band in the region of 2.2-2.8 eV is not present at T = 10 K and at T = 300 K in case of the ITO/SGL substrate used. This could be expected because strong red and green bands do not tend to co-exist [26,33].

The broad and structureless green luminescent band is mostly reported as an intrinsic defect level due to VO [34,35] or VZn [36] or both, acting as a donor-deep-acceptor pair [37]. Although controversial, the band is most likely a native complex defect of zinc vacancy involving Zni, OZn, and VO [26]. The origin of another visible Gaussian band, the red band in region of 1.5-2.0 eV, is attributed to interstitial-type defects like Zni, Oi [15,18] while PL bands between the red and the green band are commonly attributed to Oi [18,38-40]. Without a comprehensive study additional to PL spectroscopy, the defect identification remains speculative [15].

At room temperature (T = 300 K), for the ZnONRL grown at 550°C onto ITO/SGL, no green emission is detected, see Figure Figure44 inset. Therefore, we conclude that ZnONRL with a lower content of defects can be deposited using the ITO instead of SGL substrates, however, such a growth mechanism of the ZnONRL onto the ITO remains unclear. It may be speculated that a more homogenious lateral heat distribution may be responsible for the significant improvement of the NBE to red band intensity ratio (INBE/IRED) in the case of using the ITO/SGL substrate for deposition of ZnONR. Another speculation may be that ITO acts as a barrier, restraining the diffusion of some elements, e.g., sodium from the SGL glass during high-temperature spray process as it has been recorded by X-ray photoelectron spectroscopy for the CSP-deposited CuInS2 films [41]. In such a case, borosilicate glass could be a suitable replacement for the SGL substrate. Whatever the reason might be, ITO-covered substrates are preferred in order to achieve ZnONRL with high crystal quality during the CSP process. This observation is of significant importance due to the fact that for many electronic applications including solar cells, a conductive and transparent material, such as ITO, is required as the substrate material.

Effect of the growth temperature on PL properties of ZnONRL

From our previous study, it is known that the increase of TG from 480°C up to 550°C minimizes the intensity of the green PL band at 300 K [25]. The spectra recorded at T = 10 K (Figure (Figure5)5) reveal that an increase of TG from 480°C up to 550°C results in a PL spectra with significantly increased excitonic intensity, showing FWHM of 4.5 meV for ZnONRL grown at TG = 550°C onto ITO/SGL substrate. Such low values of FWHM (4.5 meV) can be correlated to a very low concentration of defects [42]. In addition, the increase of the growth temperature of ZnONRL results in an increase of the ratio of NBE to red band intensity (the red band is not shown in Figure Figure5).5). The INBE/IRED emission ratio increases as follows: 34, 39, and 160, illustrated by spectrum A, B, and C (in Figure Figure5),5), respectively. This is an indication of significant change in the defect composition in the ZnONRL and an increase of the crystal quality due to an increase of the growth temperature of ZnONRL. According to SEM study, the characteristic morphology of the samples changes with different TG. The SEM image in Figure Figure3a3a is a characteristic of ZnONRL grown at TG = 550°C. A significantly lower surface-to-volume area (no quantitative calculations were made) could be estimated from Figure Figure3b,3b, presenting the SEM image of ZnONRL deposited at TG = 480°C. At the same time, an increase of the excitonic PL band was registered without a decrease of the FWHM of the fitted peaks (Figure (Figure5,5, spectra A-C). Therefore, the increase of the intensity of the excitonic band could be due to a higher surface-to-volume ratio of the ZnONRL, in addition to an increased crystal quality. A similar effect was described for the electrochemically synthesized ZnO nanowires [20].

Figure 5
Excitonic photoluminescence spectra at 10 K of ZnO nanorod layers deposited at different growth temperatures. The growth temperature is kept at 480°C, 530°C, or 550°C, illustrated by spectrum A, B, and C, respectively. The ZnO ...

In connection with the results in the Effect of the substrate on PL properties of ZnONRL section, higher TG of 550°C and the ITO/SGL substrates are preferred for the deposition of ZnONRL in order to achieve high optical quality by the CSP method. The best samples were grown at 550°C onto ITO/SGL substrate, showing NBE emission only. Although, no significant reduction in FWHM is observed while using a higher growth temperature of 550°C, an apparent shift of the main NBE peak at approximately 3.360 eV towards higher energy could be an indicator of additional transitions. The high ratio of INBE to IVISIBLE emissions alone, although widely reported as an indication of good [43] or even excellent optical quality [7,44], may not be enough to characterize the purity of ZnONRL [15,43]. However, the resolvable fine structure of the excitonic PL emission could be taken as an indication of a relatively high crystal quality of the CSP deposited ZnONRL.

Effect of the spray rate on PL properties of ZnONRL

The effect of the variation in the spray rate on PL properties of ZnONRL is presented as Figure Figure6.6. A decrease in the spray rate from 6.2 ml/min down to 1.2 ml/min increases the intensity of the exciton peak at 3.358-3.360 eV.

Figure 6
Excitonic photoluminescence spectra at T = 10 K of ZnO nanorod layers deposited at different spray rates. The layers are deposited from aqueous solutions onto ITO/SGL substrates at 550°C with spray rate of 1.2, 2.2, and 6.2 ml/min, illustrated ...

The rise in the intensity of the peaks could be correlated to a longer deposition period, hence, a lower growth rate. In addition, the FWHM of the main peak decreases from 4.0 meV down to 2.2 meV, accompanied by a small shift from 3.360 eV to 3.358 eV in the exciton peak position. A shift in the position of a defect-bound exciton is a clear indication of a change in the type of the dominant impurity in the ZnONRL, while a smaller FWHM is a sign of increased crystal quality. For comparison, peak widths of 6-9 meV and 4.7 meV are reported for ZnONRL grown by hydrothermal method with post-deposition annealing [15] and thermal evaporation and vapor-phase transport [7], respectively. A FWHM of 1 meV is characteristic of the excitonic peak at 3.360 eV reported for a single crystal MOCVD-deposited ZnONRL, measured at 3.4 K [31]. The PL intensity in a log-scale reveals a free exciton peak at 3.378 eV appearing only at a spray rate of 1.2 ml/min (see Figure Figure66 inset), providing confirmation that a low defect density is obtained in ZnONRL [45]. Thus, in addition to high growth temperatures, low spray rates are preferred for CSP deposition of ZnONRL in case aqueous solutions are used.

Effect of solvent type on PL properties of ZnONRL

The effect of the use of different solvents on the PL properties of ZnONRL is presented as Figure Figure7.7. An exciton peak at 3.363 eV is observed only when aqueous solutions are used for deposition of ZnONRL. A shallow donor impurity corresponding to an excitonic peak at approximately 3.363 eV has been correlated to hydrogen impurity by many authors, see for example [29]. However, we can present no proof for hydrogen incorporation in this study, thus, it will not be considered further.

Figure 7
Normalized photoluminescence spectra of ZnO nanorod layers deposited using different solvents. The layers are deposited onto ITO/SGL substrate at 480°C from aqueous or alcoholic solution, illustrated by spectrum A and B, respectively. Spray rate ...

In case the alcoholic solvent is used, the excitonic band intensity increases approximately 30 times. The PL intensity ratio INBE/IRED increases from 34 in case of aqueous up to 294 in case alcoholic solution is used. This observation could be explained taking into account a similar observation from the effect of the TG (Effect of the growth temperature on PL properties of ZnONRL section). The use of an alcoholic solution results in a smaller spray droplet size, leading to a more homogeneous distribution of the sprayed solution over the substrate, compared to an aqueous solution. In addition to a smaller droplet size, the high volatility of the alcoholic solvent is very likely to cause a lower rate of the substrate cooling. Thus, a higher value of the effective growth temperature is expected in the reaction zone of pyrolysis, resulting in a somewhat higher growth temperature than the stated TG. This can be discussed in the following.

Due to the fact that the PL spectrum A in Figure Figure77 coincides with spectrum A in Figure Figure5,5, we can see that the use of an alcoholic solution instead of an aqueous solution increases the NBE band intensity (approximately × 30) in ZnONRL deposited at 480°C (Figure (Figure7).7). Similar effect has been observed while increasing the TG from 480°C up to 550°C (Figure (Figure5).5). In Effect of the growth temperature on PL properties of ZnONRL section, we tentatively attributed this effect to an increased surface-to-volume ratio of the ZnONRL. Similarly, the ZnONRL grown at 480°C from alcoholic solution (see SEM image in Figure Figure3c)3c) shows a significantly increased surface-to-volume ratio compared to ZnONRL grown at 480°C from aqueous solution (see Figure Figure3b).3b). Therefore, one possible cause of a higher NBE intensity of spectrum B compared to spectrum A in Figure Figure7,7, could be a higher surface-to-volume ratio, in addition to improved crystal quality.

Although the density of rods and the aspect ratio is known to increase when deposited from alcoholic solutions [46], the effect of the temperature cannot be overlooked either in the sense of an increased NBE intensity. As a result, it can be concluded that a lower TG or a higher spray rate is acceptable for the CSP deposition of the ZnONRL in case an alcoholic solution is used, compared to the TG and spray rates used for aqueous solutions (Effect of the growth temperature on PL properties of ZnONRL and Effect of the spray rate on PL properties of ZnONRL sections). The use of an alcoholic instead of aqueous solution could be applied in order to achieve a higher surface-to-volume ratio at a similar TG. It must be pointed out, however, that the PL of the ZnONRL deposited at a low spray rate (1.2 ml/min) from aqueous solution was superior to all considered samples in sense of narrow NBE peaks (Effect of the spray rate on PL properties of ZnONRL section).

Conclusions

We report photoluminescence properties in as-deposited ZnO nanorod layers (ZnONRL), grown via fast and low-cost pneumatic CSP method in air. The results indicate that a good crystal quality can be achieved, while ZnONRL with the best optical quality were deposited at a growth temperature of 550°C using ITO/SGL substrate. No green or red emission was detected for these samples, measured at 10 K. In addition, green emission is absent at 300 K for the best samples. The prevalence of the bound exciton transitions suggests a low defect density in our best ZnONRL. Low spray rates (1.2 ml/min) are recommended in case aqueous solution is sprayed, otherwise alcoholic solution is preferred for the deposition of ZnONRL. Lower substrate temperature is acceptable in case alcoholic solution is used, in order to achieve comparable crystal quality, compared to the use of aqueous solution. At T = 10 K, fitted excitonic peak widths (FWHM) are 2-5 meV. For comparison, peak widths of 6-9 meV are reported for ZnONRL grown by hydrothermal method with post-deposition annealing [15]. These results indicate that the quality of the spray-deposited ZnONRL is superior compared to other solution-based methods in the sense of photoluminescence properties. The results of this study imply that the spray-deposited ZnONRL is sufficient for the use as a transparent window layer in an ETA solar cell and for applications to other low-cost photonic devices at room temperature.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

EK carried out photoluminescence experiments, analysis, and interpretation of experimental results and writing of major part of paper, TR carried out photoluminescence experiments, TD designed and deposited ZnO nanorods, JK provided valuable theoretical discussions, AM provided valuable experimental discussions, VM carried out SEM study, MK designed the study, revised the manuscript, provided motivation and discussions. All authors read and approved the final version of the manuscript.

Acknowledgements

The study is financially supported by: Estonian Ministry of Education and Research (SF0140092s08) and Estonian Science Foundation grants: ETF8509, ETF6954, and ETF8282.

References

  • Look DC, Coskun C, Claflin B, Farlow GC. Electrical and optical properties of defects and impurities in ZnO. Physica B: Condensed Matter. 2003;340-342:32–38.
  • Chen TT, Cheng CL, Fu SP, Chen YF. Photoelastic effect in ZnO nanorods. Nanotechnology. 2007;18:225705. doi: 10.1088/0957-4484/18/22/225705. [Cross Ref]
  • Könenkamp R, Word RC, Godinez M. Ultraviolet electroluminescence from ZnO/polymer heterojunction light-emitting diodes. Nano Lett. 2005;5:2005–2008. doi: 10.1021/nl051501r. [PubMed] [Cross Ref]
  • Kim DC, Han WS, Cho HK, Kong BH, Kim HS. Multidimensional ZnO light-emitting diode structures grown by metal organic chemical vapor deposition on p-Si. Appl Phys Lett. 2007;91:231901. doi: 10.1063/1.2820385. [Cross Ref]
  • Zhou H, Wissinger M, Fallert J, Hauschild R, Stelzl F, Klingshirn C, Kalt H. Ordered, uniform-sized ZnO nanolaser arrays. Appl Phys Lett. 2007;91:181112. doi: 10.1063/1.2805073. [Cross Ref]
  • Ji LW, Peng SM, Su YK, Young SJ, Wu CZ, Cheng WB. Ultraviolet photodetectors based on selectively grown ZnO nanorod arrays. Appl Phys Lett. 2009;94:203106. doi: 10.1063/1.3141447. [Cross Ref]
  • Li C, Fang GJ, Liu NH, Li J, Liao L, Su FH, Li GH, Wu XG, Zhao XZ. Structural, photoluminescence, and field emission properties of vertically well-aligned ZnO nanorod arrays. J Phys Chem C. 2007;111:12566–12571. doi: 10.1021/jp0737808. [Cross Ref]
  • Wang RH, Xin JH, Tao XM, Daoud WA. ZnO nanorods grown on cotton fabrics at low temperature. Chem Phys Lett. 2004;398:250–255. doi: 10.1016/j.cplett.2004.09.077. [Cross Ref]
  • Yang Z, Li LM, Wan Q, Liu QH, Wang TH. High-performance ethanol sensing based on an aligned assembly of ZnO nanorods. Sensors and Actuators B-Chemical. 2008;135:57–60. doi: 10.1016/j.snb.2008.07.016. [Cross Ref]
  • Liu FT, Gao SF, Pei SK, Tseng SC, Liu CHJ. ZnO nanorod gas sensor for NO2 detection. J Taiwan Inst Chem Eng. 2009;40:528–532. doi: 10.1016/j.jtice.2009.03.008. [Cross Ref]
  • Chen JY, Sun KW. Growth of vertically aligned ZnO nanorod arrays as antireflection layer on silicon solar cells. Sol Energy Mater Sol Cells. 2010;94:930–934. doi: 10.1016/j.solmat.2010.01.005. [Cross Ref]
  • Tena-Zaera R, Ryan MA, Katty A, Hodes G, Bastide S, Lévy-Clément C. Fabrication and characterization of ZnO nanowires/CdSe/CuSCN eta-solar cell. C R Chim. 2006;9:717–729. doi: 10.1016/j.crci.2005.03.034. [Cross Ref]
  • Baxter JB, Aydil ES. Dye-sensitized solar cells based on semiconductor morphologies with ZnO nanowires. Sol Energy Mater Sol Cells. 2006;90:607–622. doi: 10.1016/j.solmat.2005.05.010. [Cross Ref]
  • Krunks M, Kärber E, Katerski A, Otto K, Acik IO, Dedova T, Mere A. Extremely thin absorber layer solar cells on zinc oxide nanorods by chemical spray. Sol Energy Mater Sol Cells. 2010;94:1191–1195. doi: 10.1016/j.solmat.2010.02.036. [Cross Ref]
  • Tam KH, Cheung CK, Leung YH, Djurišić AB, Ling CC, Beling CD, Fung S, Kwok WM, Chan WK, Phillips DL, Ding L, Ge WK. Defects in ZnO nanorods prepared by a hydrothermal method. J Phys Chem B. 2006;110:20865–20871. doi: 10.1021/jp063239w. [PubMed] [Cross Ref]
  • Bekeny C, Voss T, Gafsi H, Gutowski J, Postels B, Kreye M, Waag A. Origin of the near-band-edge photoluminescence emission in aqueous chemically grown ZnO nanorods. J Appl Phys. 2006;100:104317. doi: 10.1063/1.2390548. [Cross Ref]
  • Wu LL, Wu YS, Pan XR, Kong FY. Synthesis of ZnO nanorod and the annealing effect on its photoluuminescence property. Optical Materials. 2006;28:418–422. doi: 10.1016/j.optmat.2005.03.007. [Cross Ref]
  • Cross RBM, De Souza MM, Narayanan EMS. A low temperature combination method for the production of ZnO nanowires. Nanotechnology. 2005;16:2188–2192. doi: 10.1088/0957-4484/16/10/035. [PubMed] [Cross Ref]
  • Xiang B, Wang PW, Zhang XZ, Dayeh SA, Aplin DPR, Soci C, Yu DP, Wang DL. Rational synthesis of p-type zinc oxide nanowire arrays using simple chemical vapor deposition. Nano Lett. 2007;7:323–328. doi: 10.1021/nl062410c. [PubMed] [Cross Ref]
  • Voss T, Bekeny C, Gutowski J, Tena-Zaera R, Elias J, Lévy-Clément C, Mora-Sero I, Bisquert J. Localized versus delocalized states: Photoluminescence from electrochemically synthesized ZnO nanowires. J Appl Phys. 2009;106:054304. doi: 10.1063/1.3211294. [Cross Ref]
  • Hung CH, Whang WT. A novel low-temperature growth and characterization of single crystal ZnO nanorods. Mater Chem Phys. 2003;82:705–710. doi: 10.1016/S0254-0584(03)00331-6. [Cross Ref]
  • Dedova T, Krunks M, Grossberg M, Volobujeva O, Acik IO. A novel deposition method to grow ZnO nanorods: Spray pyrolysis. Superlattices Microstruct. 2007;42:444–450. doi: 10.1016/j.spmi.2007.04.010. [Cross Ref]
  • Dedova T, Volobujeva O, Klauson J, Mere A, Krunks M. ZnO nanorods via spray deposition of solutions containing zinc chloride and thiocarbamide. Nanoscale Res Lett. 2007;2:391–396. doi: 10.1007/s11671-007-9072-6. [PMC free article] [PubMed] [Cross Ref]
  • Krunks M, Dedova T, Oja Açik I. Spray pyrolysis deposition of zinc oxide nanostructured layers. Thin Solid Films. 2006;515:1157–1160. doi: 10.1016/j.tsf.2006.07.134. [Cross Ref]
  • Krunks M, Dedova T, Kärber E, Mikli V, Oja Acik I, Grossberg M, Mere A. Growth and electrical properties of ZnO nanorod arrays prepared by chemical spray pyrolysis. Physica B. 2009;404:4422–4425. doi: 10.1016/j.physb.2009.09.014. [Cross Ref]
  • Özgür Ü, Alivov YI, Liu C, Teke A, Reshchikov MA, Dogan S, Avrutin V, Cho SJ, Morkoc H. A comprehensive review of ZnO materials and devices. J Appl Phys. 2005;98:041301. doi: 10.1063/1.1992666. [Cross Ref]
  • Chen SJ, Liu YC, Lu YM, Zhang JY, Shen DZ, Fan XW. Photoluminescence and Raman behaviors of ZnO nanostructures with different morphologies. J Cryst Growth. 2006;289:55–58. doi: 10.1016/j.jcrysgro.2005.10.137. [Cross Ref]
  • Zhang R, Yin PG, Wang N, Guo L. Photoluminescence and Raman scattering of ZnO nanorods. Solid State Sciences. 2009;11:865–869. doi: 10.1016/j.solidstatesciences.2008.10.016. [Cross Ref]
  • Meyer BK, Alves H, Hofmann DM, Kriegseis W, Forster D, Bertram F, Christen J, Hoffmann A, Strassburg M, Dworzak M, Haboeck U, Rodina AV. Bound exciton and donor-acceptor pair recombinations in ZnO. Physica Status Solidi B-Basic Research. 2004;241:231–260. doi: 10.1002/pssb.200301962. [Cross Ref]
  • Teke A, Özgür Ü, Doğan S, Gu X, Morkoç H, Nemeth B, Nause J, Everitt HO. Excitonic fine structure and recombination dynamics in single-crystalline ZnO. Phys Rev B. 2004;70:195207.
  • Zhang BP, Binh NT, Wakatsuki K, Segawa Y, Kashiwaba Y, Haga K. Synthesis and optical properties of single crystal ZnO nanorods. Nanotechnology. 2004;15:S382–S388. doi: 10.1088/0957-4484/15/6/012. [Cross Ref]
  • Liu YL, Liu YC, Feng W, Zhang JY, Lu YM, Shen DZ, Fan XW, Wang DJ, Zhao QD. The optical properties of ZnO hexagonal prisms grown from poly (vinylpyrrolidone)-assisted electrochemical assembly onto Si(111) substrate. J Chem Phys. 2005;122:174703. doi: 10.1063/1.1883633. [PubMed] [Cross Ref]
  • Studenikin SA, Golego N, Cocivera M. Fabrication of green and orange photoluminescent, undoped ZnO films using spray pyrolysis. J Appl Phys. 1998;84:2287–2294. doi: 10.1063/1.368295. [Cross Ref]
  • Leiter FH, Alves HR, Hofstaetter A, Hofmann DM, Meyer BK. The oxygen vacancy as the origin of a green emission in undoped ZnO. Physica Status Solidi B-Basic Research. 2001;226:R4–R5. doi: 10.1002/1521-3951(200107)226:1<R4::AID-PSSB99994>3.0.CO;2-F. [Cross Ref]
  • Leiter F, Alves H, Pfisterer D, Romanov NG, Hofmann DM, Meyer BK. Oxygen vacancies in ZnO. Physica B: Condensed Matter. 2003;340-342:201–204.
  • Kohan AF, Ceder G, Morgan D, Van de Walle CG. First-principles study of native point defects in ZnO. Phys Rev B. 2000;61:15019–15027. doi: 10.1103/PhysRevB.61.15019. [Cross Ref]
  • Guo B, Qiu ZR, Wong KS. Intensity dependence and transient dynamics of donor-acceptor pair recombination in ZnO thin films grown on (001) silicon. Appl Phys Lett. 2003;82:2290–2292. doi: 10.1063/1.1566482. [Cross Ref]
  • Du G, Yang Y, Li T, Xu B. Preparation of polymorphic ZnO with strong orange luminescence. J Mater Sci. 2010;45:1464–1468. doi: 10.1007/s10853-009-4102-7. [Cross Ref]
  • Kim YJ, Shang HM, Cao GZ. Growth and characterization of 001 ZnO nanorod array on ITO substrate with electric field assisted nucleation. J Sol-Gel Sci Technol. 2006;38:79–84. doi: 10.1007/s10971-006-5731-9. [Cross Ref]
  • Chandrinou C, Boukos N, Stogios C, Travlos A. PL study of oxygen defect formation in ZnO nanorods. Microelectron J. 2009;40:296–298. doi: 10.1016/j.mejo.2008.07.024. [Cross Ref]
  • Katerski A, Mere A, Kazlauskiene V, Miskinis J, Saar A, Matisen L, Kikas A, Krunks M. Surface analysis of spray deposited copper indium disulfide films. Thin Solid Films. 2008;516:7110–7115. doi: 10.1016/j.tsf.2007.12.027. [Cross Ref]
  • Tena-Zaera R, Elias J, Lévy-Clément C, Bekeny C, Voss T, Mora-Sero I, Bisquert J. Influence of the Potassium Chloride Concentration on the Physical Properties of Electrodeposited ZnO Nanowire Arrays. J Phys Chem C. 2008;112:16318–16323. doi: 10.1021/jp804563a. [Cross Ref]
  • Ghosh R, Fujihara S, Basak D. Studies of the optoelectronic properties of ZnO thin films. J Electron Mater. 2006;35:1728–1733. doi: 10.1007/s11664-006-0226-6. [Cross Ref]
  • Park WI, Kim DH, Jung SW, Yi GC. Metalorganic vapor-phase epitaxial growth of vertically well-aligned ZnO nanorods. Appl Phys Lett. 2002;80:4232–4234. doi: 10.1063/1.1482800. [Cross Ref]
  • Zhou HJ, Fallert J, Sartor J, Dietz RJB, Klingshirn C, Kalt H, Weissenberger D, Gerthsen D, Zeng HB, Cai WP. Ordered n-type ZnO nanorod arrays. Appl Phys Lett. 2008;92:132112. doi: 10.1063/1.2907197. [Cross Ref]
  • Dedova T, Krunks M, Mere A, Klauson J, Volobujeva O. In: Zinc Oxide and Related Materials; Warrendale. Christen J, Jagadish C, Look DC, Yao T, Bertram F, editor. Materials Research Society; 2007. Preparation of shape and size-controlled zinc oxide nanostructures by chemical spray pyrolysis technique; pp. 359–365.

Articles from Nanoscale Research Letters are provided here courtesy of Springer
PubReader format: click here to try

Formats:

Related citations in PubMed

See reviews...See all...

Cited by other articles in PMC

See all...

Links

  • MedGen
    MedGen
    Related information in MedGen
  • PubMed
    PubMed
    PubMed citations for these articles

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...