Nanoscale Res Lett. 2009; 4(8): 948–954.
Published online Apr 25, 2009. doi:  10.1007/s11671-009-9317-7
PMCID: PMC2893893

Ultra-fast Microwave Synthesis of ZnO Nanowires and their Dynamic Response Toward Hydrogen Gas

Abstract

Ultra-fast and large-quantity (grams) synthesis of one-dimensional ZnO nanowires has been carried out by a novel microwave-assisted method. High purity Zinc (Zn) metal was used as source material and placed on microwave absorber. The evaporation/oxidation process occurs under exposure to microwave in less than 100 s. Field effect scanning electron microscopy analysis reveals the formation of high aspect-ratio and high density ZnO nanowires with diameter ranging from 70 to 80 nm. Comprehensive structural analysis showed that these ZnO nanowires are single crystal in nature with excellent crystal quality. The gas sensor made of these ZnO nanowires exhibited excellent sensitivity, fast response, and good reproducibility. Furthermore, the method can be extended for the synthesis of other oxide nanowires that will be the building block of future nanoscale devices.

Keywords: ZnO, Microwave synthesis, Nanowires, FESEM, TEM, XPES, H2gas sensor

Introduction

Fabrication of nanowires has received remarkable attention as these one dimensional (1D) nanostructures provide an ideal system to investigate the dependence of transport properties on size confinement [1]. Nanowires/nanorods are also expected to play an important role as active components or interconnects in fabricating nanoscale electronics and optoelectronics [2-6]. Zinc oxide (ZnO), a wide band-gap (3.37 eV) semiconductor, is a potentially important material. The naturally high surface-to-volume ratio of quasi 1D ZnO nanowires has made it a contender for chemical and biological sensors. In order to explore these applications, availability in large quantities is necessary. In this regard, various synthesis methods have been explored to fabricate ZnO nanowires, most of which are based on physical and chemical techniques; such as chemical vapor transport and condensation processes, metal-organic chemical vapor deposition, anodic alumina membrane templates, aqueous solution process, nonhydrolytic sol–gel processes, pulsed laser deposition, etc. [7-13]. All these methods mentioned above, however, have the disadvantages of low productivity or severe impurities from their employed assistant, so called catalyst or precursor, which bring about discomfort for their real nanodevice applications. Another limitation is the high production cost due to the complex equipment, long processing time and low growth rate. There is still an underlying question of how to scale-up nanoscale production using these approaches. In this regard, microwave heating is relatively new technique for large-scale nanowire processing which is different from existing conventional process.

Hydrogen is a hopeful potential fuel for cars, buses, and other vehicles and can be transformed into electricity in fuel cells. It is also used in medicine and space exploration as well as in the production of industrial chemicals and food products. Safety is an important issue when using the hydrogen. An explosive mixture can form if hydrogen leaks into the air from a tank or valve, posing a hazard to drivers, equipment operators, or others nearby. The present technology to detect hydrogen has numerous drawbacks which include limited dynamic range, poor reproducibility and reversibility, high power consumption and slow response, etc. Therefore, there is a need to develop new generation of metal oxide-based hydrogen gas sensors with improved performance.

In this work, we present the hydrogen gas sensing properties of ZnO nanowires prepared by a novel one-step ultra-fast microwave assisted method. The results show that the ZnO nanowire gas sensor has reversible response to H2gas. The work demonstrates the possibility of developing ZnO-based low-power consumption gas sensors and extending their applications.

Experimental Details

Zinc oxide nanostructures were synthesized using microwave technique. A microwave susceptor was used in a modified domestic microwave oven (2.45 GHz, 1250 W) to rapidly evaporate Zn. The microwave susceptor was prepared by mixing silicon carbide powder with oxide additives. A small hole of 10 mm diameter and 3 mm depth was made at the center of its top face. Small pieces of metallic zinc flakes (2–3 mm in size) were placed in the hole. A glass container was placed at a few centimeters above the absorber to collect the ZnO powder. The temperature of the absorber during exposure to microwaves was monitored with a two-wavelength pyrometer (METI-MQ11) connected to a computer. The set-up is shown in Fig. Fig.1.1. The temperature increases rapidly and exceeds 1,650 °C in less than 100 s exposures. Massive evaporation of zinc occurs as the temperature reaches about 1,200 °C giving rise to the formation of a vapor made of ZnO nanostructure that deposit on the inner surface of the glass container placed above the absorber. The crystalline phase and morphological and structural features of the products were investigated by X-ray diffraction (XRD Shimadzu-6000) using Cu Kα(0.15418 nm) radiation, field effect scanning electron microscopy (FESEM JSM-6700F), and high-resolution transmission electron microscopy (TEM TOPCON EM-002B). XPS spectra were recorded by using an Electron Spectrometer (type VG-ESCALAB MKII) equipped with a dual (Mg/Al) X-ray source and an ion gun (type EXO5). We have used the aluminum anode (Kα, 1486.6 eV). Zn 2p, C 1s, and O 1s lines were recorded. The interdigitated Pt electrode was prepared on oxidized silicon substrate. The Pt thin film was sputtered on oxidized silicon substrate. The sputtered Pt thin film was then patterned by photolithography and dry etching. About 30 mg of ZnO nanowires dispersed in ethanol and ultrasonicated. The suspension (nanowires and ethanol) dropped onto the interdigitated Pt electrode (3–5 μm thickness). Hydrogen gas sensing measurements were carried out in a quartz tube furnace. Dry synthetic air was used as a reference gas. The gas flow was monitored by mass-flow controllers. A computerized Agilent 34970A multimeter was used for electrical measurements. The resistance of the samples was determined by measuring the electric current under 10 V potential differences between the two electrodes.

Figure 1
Schematic diagram of microwave-oven based reaction system used for the synthesis of ZnO nanowires

Results and Discussion

Structural Characterization

Large quantities (grams) of ZnO nanopowder were collected from the inner wall of the glass container (Fig. (Fig.1).1). Photographic images of the microwave absorber after exposing for 10 and 25 s to microwave are shown in Fig. Fig.2a,2a, b. Figure Figure2c2c shows the large quantity of ZnO nanopowder obtained from a single reaction. Typical FESEM images of the as-synthesized ZnO nanowires are displayed in Fig. Fig.3at3at different magnifications. It can be observed that the nanowires are grown in high-density and large-scale with few micrometer length and diameter in the range of 70–80 nm.

Figure 2
Photographic images taken after 10 saandb25 s of exposure to microwave; andcZnO nanopowder in grams quantity
Figure 3
adLow and high magnification FESEM images of ZnO nanowires

X-ray diffraction measurements were carried out to examine the crystal structure of these nanowires. Figure Figure4shows4shows a typical XRD pattern that was indexed to wurtite hexagonal structure with lattice parametersa = 3.247 Å andc = 5.203 Å which is consistent with reported data (JCPDS, 79-0206). The average grain size (diameter) was estimated to be about 70 nm using Sherrer’s formula.

Figure 4
X-ray diffraction spectrum of ZnO nanowires

Figure Figure5a5a illustrates the morphology of a nanowire of 70 nm diameter as revealed by TEM image. The surface of the nanowires is generally smooth and free from structural dislocations as shown in Fig Fig5b.5b. The selected area electron diffraction (SAED) pattern in Fig. Fig.5c5c shows that the ZnO nanowires are single crystalline in nature and grow along the [0001] direction. A high resolution TEM (HRTEM) image in Fig. Fig.5d5d of the corresponding nanorwire is showing the distance of 0.52 nm between two lattice fringes, which represents the (0001) plane of the wurtzite hexagonal ZnO. The XRD and FESEM results are in agreement with the TEM analysis.

Figure 5
aandbLow and high magnification TEM images of ZnO nanowires,cCorresponding SAED pattern, anddHRTEM

Figure Figure66 shows Zn 2p3/2 and O 1s lines of XPS spectra of ZnO nanowires. Charge shift was corrected by fixing the Zn 2p3/2 line at 1021.8 eV [14]. The O 1s spectrum shows mainly a peak at 530.4 eV with a small shoulder at about 532.0 eV. The peak is assigned to oxygen atoms bound to Zn in ZnO while the shoulder has been assigned by many authors to the presence of moisture as its binding energy lies between 531.5 eV (OH) and 533 eV (H2O) [14-16].

Figure 6
XPS survey spectrum of ZnO nanowires:aZn 2p3/2andbO 1s lines

Growth Mechanism for the Formation of ZnO Nanowires

Zinc oxide nanowires were grown with the uniform diameter by ultrafast microwave synthesis technique. For the formation of ZnO nanowires Zn metallic particles was used as a source material. Two important factors are responsible for the growth of ZnO nanowires: the formation of crystalline nuclei and axial growth of ZnO nuclei [17]. The formation of nuclei depends on experimental parameters. We used swift microwave synthesis to grow 1D ZnO nanowires. The Zn particles were easily oxidized into ZnO when temperature surpasses to 419 °C. Owing to the fast oxidation, nanosized crystal nuclei were generated. These crystal nuclei were possibly generating sites for ZnO vapors, and thus the nanowires were most likely grown under the control of ZnO crystal growth habit. With the increase of reaction time and temperature, substantial quantity of ZnO nanowires was formed. ZnO is a polar crystal, where zinc and oxygen atoms are arranged alternatively along the c-axis and the top surface is Zn-terminated [0001] while the bottom surface is oxygen-terminated An external file that holds a picture, illustration, etc.
Object name is 1556-276X-4-948-i1.gif[18-21]. The top surfaces are Zn-terminated (0001) which are catalytically active, while the bottom surfaces are oxygen-terminated (000ī) which are chemically inert. Consequently, ZnO crystal grows fast along the direction in which the tetrahedron corners point [18]. The growth along the [0001] direction is dominated over other growth facets. This implies that the c-axis is the highest growth direction and the ZnO [0001] has the highest energy of the low-index surface which results in the formation of 1D ZnO nanowires.

Gas Sensing Performance of ZnO Nanowires

Zinc oxide nanowires synthesized by microwave-assisted process possess a large surface-to-volume ratio and high crystal quality. This makes them attractive candidates for gas and chemical sensing applications. Figure Figure7a7a illustrates a schematic diagram of the gas sensor device. Figure Figure7b7b shows a photograph of the device ready for measurement. Figure Figure8a8a shows the resistance response of the ZnO nanowires at 200 °C, as the ambient gas was changed from synthetic air to 500 (0.1%), 1000, and 1500 ppm hydrogen gas. The resistance decreases drastically upon exposure to hydrogen gas, and further decreases by increasing concentration of H2 from 500 to 1,500 ppm. The resistance recovers its initial value after H2 elimination, indicating an excellent reproducibility of these ZnO-based gas sensors. The response time for 500 ppm H2 gas was about 65 s. However, the recovery time was longer (about 148 s). These results are consistent with the expectation of higher relative response based on large surface-to-volume ratio and higher crystal quality of ZnO nanowires. The gas sensing mechanism is based on reversible chemisorption/desorption of hydrogen on the surface of ZnO nanowires. Oxygen is adsorbed on the surface of ZnO nanowire as O or O−2 by capturing electrons [22,23]. The presence of a negative charge on the surface leads to the formation of a depletion region underneath the surface and energy band bending due to the built-in electrical field directed toward the surface. The width of the depletion region is expected to change as the surface charge changes [24-27]. The reduction of the depletion region width as a result of desorption of negative species from ZnO surface was suggested to explain the increase of the excitonic emission of ZnO thin films under UV-illumination [28]. The change of ZnO resistance under exposure to hydrogen gas is still the subject of debate [29]. There are two different processes that could explain the reduction of the resistance of ZnO nanowires when exposed to hydrogen and its recovery after switching back to the initial conditions. First, the atomic hydrogen reacts with the negative oxygen species leading to its desorption and the formation of water molecule. As a result, the negative charge on the surface is reduced and so is the width of the depletion region, the energy band bending, and the corresponding energy barrier. Consequently, the conduction of the regions of the nanowires near the surface increases drastically. The process is very fast as it is controlled by desorption of the oxygen species. When the surface charge is completely removed, further change of the conductivity could occur as a result of the increase of the density of native defects such as the ionized oxygen vacancies which evolve toward the value corresponding to the thermodynamic equilibrium. Hydrogen gas is expected to react with oxygen atoms of ZnO to form water molecules, oxygen vacancies and free electrons in the conduction band. This process can be described by using Kroger and Vink notations as follows:

equation image
Figure 7
aSchematic illustration of the ZnO nanowire gas sensor device. The gap between two Pt fingers is 0.04 mm;bphotograph of the ZnO nanowire gas sensor. Gas sensor was connected to the measurement circuit using gold wires
Figure8
aResponse of a gas sensor made of ZnO nanowires at 200 °C to H2gas at different concentrations.btemperature verses sensitivity of ZnO nanowires

where, An external file that holds a picture, illustration, etc.
Object name is 1556-276X-4-948-i3.gif represents an oxygen vacancy positively ionized twice and An external file that holds a picture, illustration, etc.
Object name is 1556-276X-4-948-i4.gif is an oxygen atom on an oxygen site of ZnO lattice. The above reaction shows that the presence of hydrogen in the atmosphere leads to the increase of oxygen vacancies that act as donors by increasing the density of free electrons and the conductivity of ZnO nanowires. Our results indicate that ZnO nanowires showed a slow recovery as compared to the fast response to hydrogen exposure. This observation suggests that the adsorption of ionized oxygen species on the surface of ZnO nanowires and the re-establishment of a depletion region is slower than the process of desorption. When the H2 flow was discontinuous, oxygen molecules again adsorbed onto the ZnO surface and current decreased to the initial value. The decrease of current or recovery is controlled by diffusion and desorption of hydrogen on the surface of nanowires. Thus, the slow recovery is attributed to the desorption process of hydrogen from the nanowire surface and Pt metal surface. Finally, the sensor approached toward the equilibrium state. Figure Figure8b8b illustrates the sensitivity of ZnO nanowires at various operating temperatures. The sensitivity increases by increasing the operating temperature. At the operating temperature of 250 °C, the response of nanowires was more prominent than that of the operating temperature 150 °C and 200 °C which can be ascribed to the intensified reaction between the hydrogen and the adsorbed oxygen in the increasing temperature. Further exploration on the electrical properties of ZnO nanowires and their doping effect on the gas sensor response are underway.

Conclusion

In conclusion, single crystal ZnO nanowires were synthesized from high purity Zn metal via an ultra-fast, microwave-assisted process. The major advantage of this technique is its simplicity, low power consumption, fast growth (100 s), and large quantity (in grams) of nanowires. The ZnO nanowires have a wurtzite structure and showed a fast response and high sensitivity to hydrogen gas at 200 °C.

Acknowledgment

The authors would like to thank KFUPM for its support. Ahsanulhaq Qurashi is thankful to venture business laboratory of Toyama University for post doctoral fellowship.

References

  • Hu J, Odom TW, Leiber C. Acc. 1999. p. 435. COI number [1:CAS:528:DyaK1MXht1ShurY%3D] [Cross Ref]
  • Ahsanulhaq Q, Kim JH, Hahn YB. Nanotechnology. 2007. p. 485307. [Cross Ref]
  • Reddy NK, Ahsanulhaq Q, Kim JH, Hahn YB. Nanotechnology. 2007. p. 445710. [Cross Ref]
  • Reddy NK, Ahsanulhaq Q, Kim JH, Hahn YB. Appl. 2008. p. 043127. Bibcode number [2008ApPhL..92d3127K] [Cross Ref]
  • Reddy NK, Ahsanulhaq Q, Kim JH, Hahn YB. Europhys. 2008. p. 38001. Bibcode number [2008EL.....8138001K] [Cross Ref]
  • Reddy NK, Ahsanulhaq Q, Hahn YB. Appl. 2008. p. 083124. Bibcode number [2008ApPhL..93h3124R] [Cross Ref]
  • Lyu SC, Zhang Y, Lee JC, Ruh H, Lee JH. Chem. 2003. p. 3294. COI number [1:CAS:528:DC%2BD3sXltF2rsb4%3D] [Cross Ref]
  • Park WI, Kim DH, Jung SW, Yi GC. Appl. 2003. p. 4232. Bibcode number [2002ApPhL..80.4232P] [Cross Ref]
  • Wu GS, Xie T, Yuan XY, Li Y, Yang L, Xia YH, Zhang DL. Solid State Commun. 2005. p. 485. COI number [1:CAS:528:DC%2BD2MXjtF2gsr8%3D]; Bibcode number [2005SSCom.134..485W] [Cross Ref]
  • Zhang FD, Sun DL, Yin LJ, Yan CH, Wang MR. J. Phys. Chem. B. 2005. p. 8786. COI number [1:CAS:528:DC%2BD2MXisFOnurc%3D] [PubMed] [Cross Ref]
  • Zheng JM, Zhang DL, Li HG, Shen ZW. Chem. 2002. p. 123. COI number [1:CAS:528:DC%2BD38Xms1Gjtbc%3D]; Bibcode number [2002CPL...363..123Z] [Cross Ref]
  • Choi JH, Tabata H, Kawai T. J. Cryst. Growth. 2001. p. 493. COI number [1:CAS:528:DC%2BD3MXks1Wqs7c%3D]; Bibcode number [2001JCrGr.226..493C] [Cross Ref]
  • Ahsanulhaq Q, Umar A, Hahn YB. Nanotechnology. 2007. p. 115603. Bibcode number [2007Nanot..18k5603A] [Cross Ref]
  • J. Moulder, W.F. Stickle, P.E. Sobol, D.K. Bomben, in Handbook of X-ray Electron Spectroscopy, ed. by J. Chastain (Perkin-Elmer, Minnesota, 1992)
  • Avalle E, Santos E, Leiva A, Macagno V. Thin Solid Films. 1992. p. 7. COI number [1:CAS:528:DyaK3sXkslylug%3D%3D]; Bibcode number [1992TSF...219....7A] [Cross Ref]
  • Meng JL, Moreira de Sa PC, dos Santos PM. Appl. 1994. p. 57. COI number [1:CAS:528:DyaK2cXjtVygsbw%3D]; Bibcode number [1994ApSS...78...57M] [Cross Ref]
  • Yan C, Liu J, Liu F, Wu J, Gao K, Xue D. Nanoscale Res. 2008. p. 473. COI number [1:CAS:528:DC%2BD1cXhsVyhtrjP]; Bibcode number [2008NRL.....3..473Y] [PMC free article] [PubMed] [Cross Ref]
  • Yan C, Xue D. J. Phys. Chem. B. 2006. p. 25850. COI number [1:CAS:528:DC%2BD28Xht1Clu7bF] [PubMed] [Cross Ref]
  • Yan C, Xue D. Electrochem. 2007. p. 1247. COI number [1:CAS:528:DC%2BD2sXlslGit7o%3D] [Cross Ref]
  • Ahsanulhaq Q, Kim SH, Kim JH, Hahn YB. Mater. 2008. p. 3483. COI number [1:CAS:528:DC%2BD1cXht12lsb3P] [Cross Ref]
  • Ahsanulhaq Q, Kim JH, Reddy NK, Hahn YB. J. 2008. p. 578. COI number [1:CAS:528:DC%2BD1MXhtleqtrY%3D] [Cross Ref]
  • Wang TH, Kang SB, Ren F, Tien CL, Sadik WP, Norton PD, Pearton SJ, Lin J. Appl. 2005. p. 243503. Bibcode number [2005ApPhL..86x3503W] [Cross Ref]
  • Chang FJ, Kuo HH, Leu CI, Hon HM. Sens. Actuators B. 1994. p. 258. [Cross Ref]
  • Raju RA, Rao CNR. Sens. Actuators B. 1991. p. 305. [Cross Ref]
  • Saito S, Miyayama M, Kuomoto K, Yanagida H. J. 1985. p. 40. COI number [1:CAS:528:DyaL2MXhtFygs7o%3D] [Cross Ref]
  • L.H. Hartnagel, L.A. Dawar, K.A. Jain, C. Jagadish, Semiconducting Transparent Thin Films (IOP, Bristol, 1995)
  • Lupan O, Chui G, Chow L. Microelectron. 2007. p. 1211. COI number [1:CAS:528:DC%2BD2sXhtlOmu7vI] [Cross Ref]
  • Jin C, Tiwari A, Narayan JJR. Appl. Phys. (Berl) 2005. p. 083707. Bibcode number [2005JAP....98h3707J]
  • Wang TH, Kang SB, Ren F, Tien CL, Sadik WP, Norton PD, Pearton SJ, Lin J. Appl. 2005. p. 243503. Bibcode number [2005ApPhL..86x3503W] [Cross Ref]

Articles from Nanoscale Research Letters are provided here courtesy of Springer

Formats:

Related citations in PubMed

See reviews...See all...

Links

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...