Biomaterials. Author manuscript; available in PMC Jul 7, 2007.
Published in final edited form as:
PMCID: PMC1913191
NIHMSID: NIHMS18019

Auto-catalytic Ceria Nanoparticles Offer Neuroprotection to Adult Rat Spinal Cord Neurons

Abstract

This paper describes the evaluation of the auto-catalytic anti-oxidant behavior and biocompatibility of Cerium oxide nanoparticles for applications in spinal cord repair and other diseases of the CNS. The application of a single dose of nano-Ceria at a nano-molar concentration is biocompatible, regenerative and provides a significant neuroprotective effect on adult rat spinal cord neurons. Retention of neuronal function is demonstrated from electrophysiological recordings and the possibility of its application to prevent ischemic insult is suggested from an oxidative injury assay. A mechanism is proposed to explain the auto-catalytic properties of these nanoparticles.

Keywords: Adult spinal cord neurons, Auto-catalytic, Cerium oxide, Nanoparticle, Neuroprotection, Nerve regeneration

Introduction

In this study we have demonstrated that auto-catalytic nano-Ceria particles will enhance survival of adult spinal cord neurons in a unique, defined in vitro system. Ultra fine, non-agglomerated Cerium oxide nanoparticles (2–5 nm) were synthesized by a microemulsion process [1] for their suitability for neuroprotective applications in spinal cord injury and degenerative diseases of the central nervous system (CNS). To test the general biocompatibility and neuroprotection capability of the synthesized nanoparticles, we evaluated the activity of nano-Ceria in a novel serum-free cell culture model of adult rat spinal cord [2]. Administration of a single dose of nano-Ceria (10 nM) at the time of cell plating promotes significantly higher neuronal survival as compared to control cultures. Nanoparticle treated neurons indicated normal electrical activity as compared to the control culture to demonstrate functional biocompatibility. Nano-Ceria treated cells also had significantly higher cell survival upon hydrogen peroxide-induced oxidative injury in the adult spinal cord model system. Based on our cell culture assays, UV-visible spectroscopic studies, a hydrogen peroxide-induced oxidative injury assay and our proposed working hypothesis, we conclude that the supplementation of adult neuronal cultures with auto-catalytic Ceria nanoparticles has a significant effect in neuronal survival and retention of function.

Cerium oxide is a rare earth oxide that is found in the lanthanide series of the periodic table. It is used in various applications such as: histochemistry [3, 4] electrolytes for solid oxide fuel cells [5], ultraviolet absorbents [6], oxygen sensors [7, 8], and automotive catalytic converters [9]. Nanocrystalline Cerium oxide exhibits a blue shift in the ultra violet absorption spectrum [6], the shifting and broadening of Raman allowed modes [10] and lattice expansion as compared to bulk cerium oxide [6, 11]. It was these attributes of this material that were an early indicator that it has unique properties.

These results demonstrate that the use of nano-Ceria could prove beneficial for the in vivo repair of spinal cord neurons based on our experiments evaluating the nano-ceria in a more realistic in vitro model of spinal cord utilizing adult CNS cells. It is also anticipated that they could be good candidates for drug delivery and imaging applications. Based on the surface chemical properties of Ceria nanoparticles [12] we propose a hypothesis to explain the neuroprotective role of this material.

Experimental Section

Nanoparticle Synthesis

Cerium oxide nanoparticles were prepared by a microemulsion method. The nanosized micelles act as reactors for particle formation. The microemulsion system consisted of the surfactant, sodium bis(2-ethylhexyl) sulphosuccinate (AOT), toluene and water. All the chemicals were purchased from Aldrich Chemicals Company, Inc. Details of the synthesis are published elsewhere [1]. The particles obtained in toluene were re-dispersed in water by evaporating the toluene prior to use in the cell culture studies.

Nanoparticles Characterization

The particle morphology was studied using HRTEM. The surface chemistry of the nano-Ceria particles was studied using XPS. The Ceria nanoparticles were deposited on the carbon coated copper grid for HRTEM analysis by the dip coating method. The HRTEM images of the as prepared particles were obtained with a Philips (Tecnai Series) transmission electron microscope operating at 300 keV. The XPS data was obtained using a 5400 PHI ESCA (XPS) spectrometer. The base pressure during XPS analysis was 10−9 Torr and Mg-Kα X-ray radiation (1253.6eV) at a power of 200 watts was used. The binding energy of Au (4f7/2) at 84.0 ± 0.1 eV was used to calibrate the binding energy scale of the spectrometer. Any charging shift produced in the spectrum was corrected by referencing to the C (1s) position (284.6 eV) [13]. XPS spectra smoothening and baseline subtraction was carried out using PeakFit (Version 4) software.

Cell Culture

Surface modification of the coverslips for cell culture

The DETA (United Chemical Technologies Inc. T2910KG) films were formed by the reaction of the cleaned glass surface with a 0.1% (v/v) mixture of the organosilane in freshly distilled toluene (Fisher T2904). The DETA coated coverslips were heated to just below the boiling point of toluene, rinsed with toluene, reheated to just below the boiling temperature, and then oven dried. The detailed procedure is described elsewhere [14, 15]

Surface characterization of the coverslips

Surfaces were characterized by contact angle measurements using an optical contact angle goniometer (KSV Instruments, Cam 200) and by XPS (Fisions 220i). XPS survey scans, as well as high-resolution N 1s and C 1s scans, utilizing monochromatic Al Kα excitation, were obtained according to our previously published procedures [2, 1417].

Isolation and culture of rat spinal cord

Spinal cords were isolated from euthanized adult rats (average age was 3–4 months) and the meninges were removed from the spinal cord. One single spinal cord from an adult rat weighs 1.10 g (+/− 0.05). The harvested spinal cord was cut into small pieces and collected in cold Hibernate A [18] (www.BrainBits.com), GlutaMAX™, an antibiotic-antimycotic and B27 (Invitrogen). Next, the tissue was enzymatically digested for 30 minutes in papain (2mg/ml). The tissue was dissociated in 6 ml of fresh Hibernate A, GlutaMAX™, an antibiotic-antimycotic and B27. The 6 ml cell suspension was layered over a 4 ml step gradient (Optipep diluted 0.505: 0.495 (v/v) with Hibernate A/ GlutaMAX™ / antibiotic-antimycotic/ B27 and then made to 15%, 20%, 25% and 35% (v/v) in Hibernate A/ GlutaMAX™/ antibiotic-antimycotic/ B27) followed by centrifugation for 15 min, using 800g, at 4°C. The top 7 ml of the supernatant was aspirated. The next 2.75 ml from the major band and below was collected and diluted in 5ml Hibernate A/ GlutaMAX™/ antibiotic-antimycotic/ B27 and centrifuged at 600 g for 2 minutes. The pellet was resuspended in Hibernate A/ GlutaMAX™/ antibiotic-antimycotic/ B27, and after a second centrifugation, the pellet was resuspended in the culture medium. Approximately 12,000–13,000 live cells are harvested from one adult rat spinal cord. 1000 cells were plated on each coverslip (22 X 22 mm2) at 2 cells/mm2. The culture medium was changed completely after the first 2 days in culture and thereafter half of the medium was changed every four days [2, 19]. A molecular Probe's L-3224 Live/Dead Assay kit was used for the live-dead assays [16].

Immunocytochemistry for quantification of neuronal and glial cells in control and nanoparticle treated culture

Rabbit anti-neurofilament M polyclonal antibody, 150 kD, (Chemicon, AB1981, diluted 1:100) and mouse anti-GFAP monoclonal antibody (Chemicon MAB360, diluted 1:400), were used for staining the neuronal and gial cells. The method for immunostaining is described in detail elsewhere [2].

Electrophysiology of nanoparticle treated culture

Voltage clamp and current clamp experiments were performed with a Multiclamp 700A (Axon, Union City, CA) amplifier. Signals were filtered at 3 kHz and digitized at 20 kHz with an Axon Digidata 1322A interface. Data recording and analysis was performed with pClamp 8 (Axon) software. The detailed protocols are documented in our previous work [2, 16].

Results and Discussion

A microemulsion process was used to synthesize the cerium oxide nanoparticles (Figure 1a) and they were characterized for morphology and surface chemistry by high-resolution transmission electron microscopy (HRTEM) and X-ray photoelectron spectroscopy (XPS). HRTEM indicated the formation of uniformly distributed, non-agglomerated nanoparticles of Cerium oxide in the range of 3–5nm as shown in the image in Figure 1b. Figure 1c shows a XPS spectrum that indicates a mixed valence state (Ce3+ and Ce4+) for the synthesized Cerium oxide nanoparticles. These results are similar to our previously published results [1, 12, 20].

Figure 1
Synthesis and Characterization of Cerium oxide Nanoparticles. (a) Outline of the microemulsion technique to synthesize the nano-Ceria (b) XPS analysis of synthesized Cerium oxide nanoparticles showing the presence of both Ce3+ and Ce4+ valence states ...

The in vitro studies with the synthesized nanoparticles were carried out in a serum-free cell culture model of adult rat spinal cord (Figure 2) which has been shown to promote growth and long-term survival of dissociated adult rat spinal cord neurons [2]. This system consists of a patternable [15], non-biological, cell growth promoting organosilane substrate, N-1 [3-(trimethoxysilyl) propyl] diethylenetriamine (DETA) [16, 17, 21, 22], coated on a glass surface combined with an empirically derived, novel serum-free medium and a reproducible cellular isolation and pre-plating methodology. The serum-free medium consisted of neurobasal A supplemented with B27 [23], GlutaMAX™, acidic fibroblast growth factor, heparin sulphate, neurotrophin-3, neurotrophin-4, ciliary neurotrophic factor (CNTF), brain derived neurotrophic factor, glial derived neurotrophic factor, cardiotrophin-1, vitronectin and an antibiotic-antimycotic (Figure 2b). The quality of the surface modified coverslips used for cell culture was monitored using static contact angle measurements and XPS analysis as previously described [2, 14, 16, 17]. Stable contact angles (40.64° ± 2.9/mean ± SD) throughout the study indicated high reproducibility and quality of the DETA coatings and were similar to previously published results [2, 14, 16, 17, 24]. Based on the ratio of the N 1s (401 and 399 eV) and the Si 2p3/2 peaks, XPS measurements indicated that a monolayer of DETA (Figure 2c) was formed on the coverslips [2, 14, 16, 17]. The cell isolation process from dissected adult rat spinal cord is briefly described in the methods.

Figure 2
Adult Rat Spinal Cord Culture (a) Isolation of adult rat spinal cord cells from the whole cord (b) Development of serum-free culture medium using various growth factors (c) Surface modification of the glass cover slips for cell culture.

The outline of the cell isolation and cell plating is shown in Figure 2a and documented in detail in our previous work [2]. In each experiment, an equal volume of the cell suspension (1000 live cells at a density of 2 cells/mm2) was plated on each coverslip. Of the total number of coverslips plated with cells, half of the coverslips were used for control cultures and the other half received a single dose of 10nM nano-Ceria at the time of cell plating. At two different time intervals, day 15 and day 30, live-dead assays and neuron-glia immunostaining assays were conducted to quantify cell viability and the surviving cell types in both the control and nano-Ceria treated cultures. A student’s T-test was used for statistical analysis. The results are expressed as mean ± SE, n = 6, where n stands for number of coverslips. The total number of coverslips used for these assays were drawn from six different experiments. Live-dead cell assays (Figure 3a) indicated a significantly higher cell survival at day 15 (617 ± 34, n = 6) and at day 30 (472 ± 35, n = 6) in nano-Ceria treated cultures as compared to the control cultures at day 15 (479 ± 37, n = 6) and day 30 (328 ± 32, n = 6). We also observed a significantly lower cell death at day 15 (59 ± 7, n = 6) and day 30 (48 ± 7, n = 6) in nano-Ceria treated cultures as compared to the control cultures on day 15 (110 ± 9, n = 6) and day 30 (72 ± 8, n = 6). Neurons and glial cells were identified by immunoreactivity for neurofilament 150 (neuronal marker) and glial fibrilliary acidic protein (GFAP) (glial marker) antibodies respectively. The neuronal population was significantly higher in nano-Ceria treated cultures at day 15 (191 ± 40, n = 6) and at day 30 (221 ± 12, n = 6) compared to the control cultures on day 15 (71 ± 26, n = 6) and day 30 (148 ± 9, n = 6). There was no significant difference in glial cell population or populations of cells which stained for both neuron and glial markers in treated cultures compared to control cultures at either time interval (Figure 3b). Electrical activities of the nano-Ceria treated cultures were assessed using patch-clamp electrophysiology at day 30 in culture. The treated neurons expressed voltage dependent inward and outward currents (Figure 4a) and generated single action potentials (Figure 4b), similar to that observed for the controls and in other adult rat CNS cultures [2, 25].

Figure 3
Live-Dead Assay and Neuron-Glial Cell Assay Studies of Control and nano-Ceria Treated Cultures of Adult Rat Spinal Cord (a) Live-dead cell assays indicated that nano-Ceria treated cultures had significantly higher cell survival and significantly less ...
Figure 4
Voltage-clamp recording from a treated culture at day 30 (left) Current clamp recording indicating a single action potential in a nano-Ceria treated culture at day 30 (right).

We propose that the presence of the mixed valence states of Ce3+ and Ce4+ on the surface of the nano-Ceria act as an anti-oxidant that allow the nanoparticles to scavenge free radicals from the culture system. Another complex set of surface chemical reactions [26] between the ions in the cell culture medium and the nano-Ceria then appear to be involved in reversing the oxidation state from Ce4+ to Ce3+. We believe that this is indicative of a cyclical regenerative, or auto-catalytic, reaction of the Ceria nanoparticles. The proposed mechanism is shown in Figure 5. To demonstrate the auto- catalytic property of the engineered nano-Ceria particles, we carried out a UV-visible spectroscopic study of a nano-Ceria sol treated with 10mM hydrogen peroxide (Figure 6). The UV-Visible spectrum of a sample of the nano-Ceria solution was used as a control (black trace in the graph). We added hydrogen peroxide to this solution and observed a shift in the spectrum to the right or to the lower energy portion of the spectrum (pink trace). In this reaction, hydrogen peroxide provides a source of hydroxyl radicals to mimic oxidative stress found in vivo. This shift is postulated to be due to a change in the oxidation state from Ce3+ to Ce4+[27]. The nano-Ceria sample treated with hydrogen peroxide was then kept in the dark for 30 days. UV-Visible spectra of these samples were then taken at day 15 and day 30 (blue and red traces for the day 15 and day 30 spectra, respectively). A gradual shift in the spectra to the left was seen over time. This gradual higher energy shift reflects the regeneration (Ce4+ →Ce3+) of the cerium oxide nanoparticles. When an additional hydrogen peroxide dose was administered to the solution on day 30, the UV-Visible spectrum again shifted to lower energy (green trace) which was followed by a gradual shift to the lower wavelength, as seen previously. The shift of the UV visible spectrum to a lower energy state on exposure to hydrogen peroxide with a recovery toward a higher energy state (Ce3+ → Ce4+ → Ce3+). This indicates that nano-ceria exhibits a mechanism in which the engineered particle provides a new material for life science applications with unprecedented antioxidant activity and pseudo-infinite half-life. The auto-regenerative anti-oxidant property of these nanoparticles appears to be the key to its neuroprotective action.

Figure 5
Schematic Detailing the Proposed Regenerative Properties of nano-Ceria and probable mechanism of Cerium oxide nanoparticles’ free radical scavenging property and auto-catalytic behavior.
Figure 6
UV-visible study of Cerium Oxide nanoparticles treated with hydrogen peroxide at different time intervals.

The auto-catalytic properties of the ceria oxide particles were further demonstrated in a hydrogen peroxide-induced oxidative injury model utilizing the adult spinal cord model system. A 100 mM hydrogen peroxide solution was added for 1h to both a control culture and a nano-Ceria treated culture at day 30. After 1h of hydrogen peroxide treatment, the cell viability was assayed using a live-dead assay kit. The nano-Ceria treated cultures had a significantly higher number of live cells (82 ± 18, n = 6) as compared to the control (29 ± 6, n = 6). We did not observe any significant difference in the number of dead cells between nano-Ceria treated (362 ± 73, n = 6) and control (309 ± 44, n = 6) cultures after hydrogen peroxide treatment. This result indicates that the nano-Ceria treated cultures had a significantly higher peroxide detoxification ability (Figure 7) and this may also be a significant indicator of its potential protection abilities after ischemic insult.

Figure 7
Results After Hydrogen Peroxide-Induced Oxidative Injury in Control and Treated Cultures of Adult Rat Spinal Cord at day 30. Live-dead cell assay after hydrogen peroxide treatment indicates that nano-Ceria treated cultures had a significantly higher number ...

Spinal cord neurons and other CNS neurons are prone to damage due to oxidative stress [28, 29] both in vitro [30] and in vivo [3133]. To maintain healthy in vitro cultures of spinal neurons and other CNS neurons, several antioxidants are generally used in culture medium. The major source of anti-oxidant molecules in serum-free neuron culture medium is the B27 supplement [23, 34]. B27 contains five antioxidants; vitamin E, vitamin E acetate, superoxide dismutase, catalase, and glutathione [23]. However, the half-life of these antioxidants is limited and they have to be replenished each time the medium is changed to maintain a healthy culture [34]. In nano-Ceria treated cultures, we observed a significant rise in neuron survival as compared to the control culture, which were supplemented only with B27. The auto-regenerative antioxidant properties of a single dose of the autocatalytic nano-Ceria in this in vitro model is the most probable explanation of the significant neuroprotective effect observed in the treated culture.

Conclusions

Based on our cell culture assays, UV-visible spectroscopic studies, hydrogen peroxide-induced oxidative injury assay and our proposed working hypothesis, we conclude that the supplementation of neuronal cultures with a single dose of the Ceria nanoparticles has a significant synergistic effect in a realistic model system of spinal cord injury. Future studies will focus on elucidating the biological mechanism of action of the nano-Ceria. The use of nano-Ceria with other antioxidants may, in the future, prove beneficial for the in vivo mitigation of ischemic events after spinal cord injury as well as possibly being a new therapeutic agent for oxidation injury in the other neurodegenerative diseases or injury.

Acknowledgments

We would like to acknowledge that support for this research were provided from the University of Central Florida as well as NIH grant number 5 RO1NS050452-03. We confirm that any aspect of the work covered in this manuscript that has involved experimental animals has been conducted with the ethical approval of all relevant bodies.

Footnotes

Publisher's Disclaimer: This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting proof before it is published in its final citable form. Please note that during the production process errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain.

References

1. Patil S, Kuiry SC, Seal S, Vanfleet R. Synthesis of nanocrystalline ceria particles for high temperature oxidation resistant coating. Journal of Nanoparticle Research. 2002 Oct;4( 5):433–8.
2. Das M, Bhargava N, Gregory C, Riedel L, Molnar P, Hickman JJ. Adult Rat Spinal Cord Culture On An Organosilane Surface In A Novel Serum-Free Medium. In Vitro Cell Dev Biol Anim. 2005;41:343–8. [PubMed]
3. Briggs RT, Drath DB, Karnovsky ML, Karnovsky MJ. Localization of NADH oxidase on the surface of human polymorphonuclear leukocytes by a new cytochemical method. J Cell Biol. 1975 Dec;67(3):566–86. [PMC free article] [PubMed]
4. Telek G, Scoazec JY, Chariot J, Ducroc R, Feldmann G, Roze C. Cerium-based histochemical damonstration of oxidative stress in taurocholate-induced acute pancreatitis in rats: A confocal laser scanning microscopic study. J Histochemistry & Cytochemistry. 1999;47(9):1201–12. [PubMed]
5. Eguchi K, Setoguchi T, Inoue T, Arai H. Electrical properties of ceria-based oxides and their application to solid oxide fuel-cells. Solid State Ionics. 1992;52( 1–3):165–72.
6. Tsunekawa S, Sivamohan R, Ohsuna T, Kasuya A, Takahashi H, Tohji K. Ultraviolet absorption spectra of CeO2 nano-particles. Materials Science Forum. 1999;315–317:439–45.
7. Izu N, Shin W, Matsubara I, Murayama N. Development of resistive oxygen sensors based on cerium oxide thick film. Journal of Electroceramics. 2004;13( 1–3):703–6.
8. Jasinski P, Suzuki T, Anderson HU. Nanocrystalline undoped ceria oxygen sensor. Sensors and Actuators B-Chemical. 2003;95( 1–3):73–7.
9. Masui T, Ozaki T, Machida K, Adachi G. Preparation of ceria-zirconia sub-catalysts for automotive exhaust cleaning. Journal of Alloys and Compounds. 2000;303:49–55.
10. Spanier JE, Robinson RD, Zhang F, Chan SW, Herman IP. Size-dependent properties of CeO2-y nanoparticles as studied by Raman scattering. Physical Review B. 2001;64:245407-1–-7.
11. Feng Z, Siu-Wai C, Spanier JE, Apak E, Qiang J, Robinson RD, Herman IP. Cerium oxide nanoparticles: size-selective formation and structure analysis. Applied Physics Letters. 2002;80:127–9.
12. Patil S, Kuiry SC, Seal S. Nanocrystalline ceria imparts better high-temperature protection. Proceedings of the Royal Society of London Series A- Mathematical Physical and Engineering Sciences. 2004 Dec 8;460( 2052):3569–87.
13. Barr TL, Seal S. On the nature of the use of adventitious carbon as binding energy standard. Journal of Vacuum Science and Technology. 1995;13A:1239–46.
14. Stenger DA, Pike CJ, Hickman JJ, Cotman CW. Surface determinants of neuronal survival and growth on self-assembled monolayers in culture. Brain Res. 1993 Dec 10;630(1–2):136–47. [PubMed]
15. Ravenscroft MS, Bateman KE, Shaffer KM, Schessler HM, Jung DR, Schneider TW, Montgomery CB, Custer TL, Schaffner AE, Liu QY, Li YX, Barker JL, Hickman JJ. Developmental neurobiology implications from fabrication and analysis of hippocampal neuronal networks on patterned silane-modified surfaces. Journal of the American Chemical Society. 1998 Dec 2;120(47):12169–77.
16. Das M, Molnar P, Devaraj H, Poeta M, Hickman JJ. Electrophysiological and morphological characterization of rat embryonic motoneurons in a defined system. Biotechnol Prog. 2003 Nov–Dec;19(6):1756–61. [PubMed]
17. Das M, Molnar P, Gregory C, Riedel L, Jamshidi A, Hickman JJ. Long-term culture of embryonic rat cardiomyocytes on an organosilane surface in a serum-free medium. Biomaterials. 2004 Nov;25(25):5643–7. [PubMed]
18. Brewer GJ, Price PJ. Viable cultured neurons in ambient carbon dioxide and hibernation storage for a month. Neuroreport. 1996 Jun 17;7(9):1509–12. [PubMed]
19. Brewer GJ. Isolation and culture of adult rat hippocampal neurons. J Neurosci Methods. 1997 Feb;71(2):143–55. [PubMed]
20. Tarnuzzer RW, Colon J, Patil S, Seal S. Vacancy engineered ceria nanostructures for protection from radiation-induced cellular damage. Nano Lett. 2005;5(12):2573–7. [PubMed]
21. Das M, Gregory CA, Molnar P, Riedel LM, Wilson K, Hickman JJ. A defined system to allow skeletal muscle differentiation and subsequent integration with silicon microstructures. Biomaterials. 2006;27:4374–80. [PubMed]
22. Kleinfeld D, Kahler KH, Hockberger PE. Controlled outgrowth of dissociated neurons on patterned substrates. J Neurosci. 1988 Nov;8(11):4098–120. [PubMed]
23. Brewer GJ, Torricelli JR, Evege EK, Price PJ. Optimized survival of hippocampal neurons in B27-supplemented Neurobasal, a new serum-free medium combination. J Neurosci Res. 1993 Aug 1;35(5):567–76. [PubMed]
24. Schaffner AE, Barker JL, Stenger DA, Hickman JJ. Investigation of the factors necessary for growth of hippocampal neurons in a defined system. J Neurosci Methods. 1995;62(1–2):111–9. [PubMed]
25. Evans MS, Collings MA, Brewer GJ. Electrophysiology of embryonic, adult and aged rat hippocampal neurons in serum-free culture. J Neurosci Methods. 1998 Jan 31;79(1):37–46. [PubMed]
26. Tsunekawa S, Sivamohan R, Ito S, Kasuya A, Fukuda T. Structural study on monosize CeO2−x nano-particles. Nanostructured Materials. 1999;11(1):141–7.
27. Djuricic B, Pickering S. Nanostructured cerium oxide: Preparation and properties of weakly-agglomerated powders. Journal of the European Ceramic Society. 1999;19( 11):1925–34.
28. Cookson MR, Shaw PJ. Oxidative stress and motor neurone disease. Brain Pathol. 1999 Jan;9(1):165–86. [PubMed]
29. Ogawa N. Free radicals and neural cell damage. Rinsho Shinkeigaku. 1994 Dec;34(12):1266–8. [PubMed]
30. Whittemore ER, Loo DT, Watt JA, Cotman CW. A detailed analysis of hydrogen peroxide-induced cell death in primary neuronal culture. Neuroscience. 1995;67(4):921–32. [PubMed]
31. Liu D, Liu J, Wen J. Elevation of hydrogen peroxide after spinal cord injury detected by using the Fenton reaction. Free Radic Biol Med. 1999 Aug;27(3–4):478–82. [PubMed]
32. Liu D, Yang R, Yan X, McAdoo DJ. Hydroxyl radicals generated in vivo kill neurons in the rat spinal cord: electrophysiological, histological, and neurochemical results. J Neurochem. 1994 Jan;62(1):37–44. [PubMed]
33. Bao F, Liu D. Hydroxyl radicals generated in the rat spinal cord at the level produced by impact injury induce cell death by necrosis and apoptosis: protection by a metalloporphyrin. Neuroscience. 2004;126(2):285–95. [PubMed]
34. Perry SW, Norman JP, Litzburg A, Gelbard HA. Antioxidants are required during the early critical period, but not later, for neuronal survival. J Neurosci Res. 2004 Nov 15;78(4):485–92. [PubMed]
PubReader format: click here to try

Formats:

Related citations in PubMed

See reviews...See all...

Cited by other articles in PMC

See all...

Links

  • Compound
    Compound
    PubChem Compound links
  • MedGen
    MedGen
    Related information in MedGen
  • PubMed
    PubMed
    PubMed citations for these articles
  • Substance
    Substance
    PubChem Substance links

Recent Activity

Your browsing activity is empty.

Activity recording is turned off.

Turn recording back on

See more...